Electronics Forum | Thu Oct 05 13:24:42 EDT 2023 | rgduval
So, a couple of things... First, you're asking about water washing a part, but, note that the manufacturer says to NOT ultrasonically clean their microphones. Those can be two different cleaning types...assembly shops using water wash may not be us
Electronics Forum | Wed Dec 06 05:50:42 EST 2023 | calebcsmt
For typical small sized circle LED panels, you can simply have a PCB routed to said circle... but when lighting fixtures are sizes 2-3 feet+, and a circular, typically how are the LEDs being spread across the radius? I can see flex LED strips being
Electronics Forum | Sun Feb 23 14:32:42 EST 2003 | davef
Sources of sulphur in PCB fabrication are: * Some locales have high H2S concentrations in the air. * Metal etching steps that use sulfuric acid or a sulfonated buffering compound may result in sulfate residues. * Sulfates can come from contact with
Electronics Forum | Wed Aug 30 16:00:42 EDT 2000 | Dave F
Russells: You can mix the two solders you mentioned, assuming by "96s" you meant "96Sn / 4Pb". If you heat the two tin / lead alloys to a liquid state, you�ll form a tin / lead solution with properties different from either of the two solders. The
Electronics Forum | Tue Apr 17 10:16:42 EDT 2001 | davef
Welcome to SMTnet. Awww, those assemblers are always whining about something. Just tell him to shut-up and build the blankin� boards. Jeesh!!! We used to have copious archives on the topic on SMTnet and our friend Brian is working his fingers t
Electronics Forum | Sat Jul 14 10:34:42 EDT 2001 | davef
This portion of SMTnet is intended for people whining about the operation of the forums and what-not. A lot of the people asking questions like your use the production forum. We don't have an air knife on our wave, but I recall some threads on SMTn
Electronics Forum | Fri Nov 12 10:00:42 EST 1999 | Dave F
Edmund, following-on from Wolfy: Back in the old days, anyone who could spell "sodder" considered "bright and shiny connections" GOOD and "dull and grainy connections" BAD. Now, "dull and grainy" connections can be either GOOD or BAD, depending on
Electronics Forum | Wed Oct 06 08:41:42 EDT 1999 | Dave F
| | Hi, | | | | Help! Could anyone help to enlighten me on this? | | | | Question: | | | | If I have a CSP/BGA package of size X by Y and the standoff gap between the component and PCB is Z, What is the maximum allowable Y/Z or X/Z that using a n
Electronics Forum | Wed Sep 22 09:25:42 EDT 1999 | Wolfgang Busko
| | i'm sure everyone has run into this at one point or another. I have a thin pcb .025 that is single up that has to be built on a pallet. does anyone have any tricks to the pallet design that will help to hold these boards down during the scree
Electronics Forum | Mon Sep 13 14:13:42 EDT 1999 | Jennifer
| Dearest Jennifer, | | Ooooops! Forgot which one I was writing - please forgive me. Ah yes, SMT and you, you see even we don't get it right. If you combined all our answers, you would get close - as close as when we get frustrated. | | And on it g