Electronics Forum | Wed Mar 20 11:55:19 EST 2002 | slthomas
Interesting. Ours failed miserably. Of course we toss everything on the stencil at the end of a shift (they are instructed to let it run down to minimal volume on the stencil as they approach quitting time) so it's not an issue. We are more concer
Electronics Forum | Thu Mar 21 13:59:24 EST 2002 | vargas_s
We are actively looking to buy a Fuji CP6 series placement machine in the used market. We constructed a questionnaire for perspective sellers trying to get as much information out of them as we can regarding possible machines (serial numbers, dates,
Electronics Forum | Sun Mar 31 10:03:25 EST 2002 | Bob
Cheers Dave, to answer some of your questions. � The component lead is copper with a tin / lead coating. The pads are standard Copper / Nickel / Gold. � The solder is standard Tin / Lead / Silver (2%) We have a lab that can determine the composition
Electronics Forum | Fri Apr 12 16:30:21 EDT 2002 | stepheno
If you are going to wavesolder the board after SMT you will have to epoxy the parts on instead of paste/reflow. I used to work for a company that squeeged it on. You will have to research component layout guidelines if you do want to wavesolder. If
Electronics Forum | Sat Apr 20 01:25:39 EDT 2002 | lysik
It is not just the rgistration fee. It is the fact that often after you register the machine you sre still denied a certian portion of service. UIC is very in check with their registration pricing. OEM's do however have a clause that says we can not
Electronics Forum | Sat Apr 20 22:50:36 EDT 2002 | lysik
I am sure the QP-132 is a more stable platform. It is a Fuki after all. My big question is why not X2 CP-6 machines. I mean you can tell by resale value of the FCM Vs the QP-132 that the QP-132 is a rock solid machine but, for such cheap money two CP
Electronics Forum | Mon Apr 15 21:27:16 EDT 2002 | djarvis
Everything we do is RF and have had no problems in the last 7 years with - Indium NC-SMQ92J, Sn63 Pb 37, 90.25% Metal, -325+500 mesh. Stencils are always 0.005" thick. However I will qualify that by adding we are an OEM and each new product may requi
Electronics Forum | Mon Apr 22 13:05:52 EDT 2002 | davef
Try: Somar Corporation, 11-2, Ginza 4-chome, Chuo-ku Tokyo 104-8109, JAPAN http://www.horiba.co.jp/ +81 3 35422151 +81 3 35422056 Not to imply there is anything wrong with Somar's material [having never used the material], just looking at an alterna
Electronics Forum | Mon May 13 16:20:10 EDT 2002 | ian
Are you refering to MacDermid Sterling Silver finish or immersion silver in general. We have had enquiries about Sterling Silver from a customer and the blurb I have read looks very good (don't most sales literature). Has anyone tried this finish? O
Electronics Forum | Thu May 09 12:29:59 EDT 2002 | dougt
So after barcoding takes place, is this info sent to the feeder or the outside world (is the feeder just a number that the pick and place machine looks for or does the feeder tell the machine what it has)? I guess if every machine and remote feeder f