| | | Netters, | | | | | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | | | | | 1. Kester 293 no clean | | | 2. 2.1 C/s for 30s to 150 C | | | 3.
Electronics Forum | Sat Mar 27 12:36:34 EST 1999 | Scott Cook
| Hi, | I have a customer who's electronic assemblies produce RF. He is insisting upon aqueuos cleaning. We switched to a no clean solder years ago and no longer have an aqueous system. | Is aqueous cleaning necessary to eliminate 'cross talk' of
Electronics Forum | Tue Mar 23 23:17:03 EST 1999 | Chris G.
| Are there many of you who are soldering through hole parts in your surface mount reflow oven? How repeatable is the process? Do you need to touch up a lot after reflow? We don't do long runs maybe 200, 300 boards max. Can you just screen print
Electronics Forum | Thu Mar 25 21:46:29 EST 1999 | C4 GSM GURU
| | Hey, all you Pro's out there I am looking for someone that has worked with the Universal FlexJet. We have been Beta testing one for a couple of months now and are having problems with interfacing optimization software with it. I would
Electronics Forum | Thu Mar 18 18:40:15 EST 1999 | Marc Ruggiero
| | | Hi folks, | | | | | | I am looking for inputs on a long-standing problem encountered in our shop: Bottom-side parts (passives) falling off in the Wave...where the only remnants of the part is a flattened glue dot of proper diameter and volum
Electronics Forum | Fri Mar 19 11:01:42 EST 1999 | Dave F
| Hi folks, | | I am looking for inputs on a long-standing problem encountered in our shop: Bottom-side parts (passives) falling off in the Wave...where the only remnants of the part is a flattened glue dot of proper diameter and volume, and somet
Electronics Forum | Wed Mar 17 17:53:12 EST 1999 | Steve Skinner
| | Does anyone have any recommendations on spray fluxers? Are there major differences between the high priced ultrasonic machines to the low priced flux/air spraying machines? We are going to be spraying an OA flux with 11% solids content. Are there
Electronics Forum | Mon Mar 15 23:00:40 EST 1999 | Dave F
| In the early days, we used screens made of stainless steel or polyester. Sometimes - after A period - the tension was not good, because A wire was broken. | Later on we started to us metal stencils, glued in A polyester screen. even than we had som
Electronics Forum | Tue Mar 16 08:38:59 EST 1999 | George Verboven (Process Engineer)
| | In the early days, we used screens made of stainless steel or polyester. Sometimes - after A period - the tension was not good, because A wire was broken. | | Later on we started to us metal stencils, glued in A polyester screen. even than we had
Electronics Forum | Fri Mar 19 08:51:57 EST 1999 | Justin Medernach
| | | After rmoving a BGA (plastic)to correct unexplained shorts | | | I installed another BGA using flux only. | | | Checking on an X Ray machine and found two shorts. | | | | | | can anyone give a good explenation ? | | | | | | Thanks | | | | |