Electronics Forum | Sat Oct 01 11:48:45 EDT 2005 | Hiram
Hello everybody, We are in the process of implementing NC process on the wave solder. We have a Sonotek XL fluxing system. Any ideas out there? Solder used: SN100C Flux options so far: 264-5 flux, 270WR VOC-free 9both from AIM solder) The flux ch
Electronics Forum | Thu Oct 27 13:22:30 EDT 2005 | moonshine
All solder pastes are worth consideration depending on your needs. What do you need to do? When you know this, run the experiment and determing what best works. I never have found a situation when/where Indium or Kester has failed to perform. This,
Electronics Forum | Thu Apr 06 16:42:44 EDT 2006 | russ
this is all good jay but would WML have to say about this paste? I'm gonna wait for his response before I do anything! I am bringing in some samples of this soon to try for myself. I have a part that the manufacturer says to run with a paste with n
Electronics Forum | Thu Apr 06 17:02:48 EDT 2006 | jbrower
I'm just dying to hear. I think this past will be a contender for us, I'd use it but I allready commited to using the Kester EM907. Maybe after the first of the year I'll look at switching to this paste. Ive never heard of a problem like that, but
Electronics Forum | Fri Apr 14 07:59:42 EDT 2006 | amol_kane
Hi russ, I am in the process of developing a "hybrid" reflow profile to solder a board that has LF BGAs and leaded solder. Have you encountered a similar situation before? if so what was the "safe" top side temp for the leaded components that was set
Electronics Forum | Tue Dec 19 16:26:24 EST 2006 | samir
Grant, Newer lead-free fluxes have 6%-10% solids content - more activator, therefore leave more "visible" residues. Old technology tin-lead fluxes got down to as low as around the 4%-6% range (I'm going off memory, so me might be wrong)... You'll
Electronics Forum | Mon Oct 08 18:21:27 EDT 2007 | mariss
We have recently acquired a Passaat SMRO-0406 oven. The manual is uninformative for oven settings. Can someone supply us with starting points for conveyor speed, Zone 1 to 4 and 5 to 8 temperature settings please? Our boards for a product we manufac
Electronics Forum | Thu Feb 07 05:18:08 EST 2008 | muarty
If there is a budget available, rather than looking at a Fuji CP7. Being issued with small strips of components would prove to be a nightmare with this style of placement machine. I would try to consider the Fuji AIM machine for use as the chipshoote
Electronics Forum | Thu Apr 10 07:47:47 EDT 2008 | ck_the_flip
Stencil design and pad layout are key. Too far apart - bad. If your pad geometry is correct, try the inverted home plate. That has worked well for me in the past. That, coupled with a 5-mil stencil. With regard to solder paste, some manufacturer
Electronics Forum | Wed May 07 10:15:46 EDT 2008 | llaerum
We are also having some issues with certain small parts. In our case this is tantalum caps and 0402 caps. We had a vendor admit after much discussion that the plating used from a particular orgin was different on the tantalums. The tehory is thatthsi