Electronics Forum | Tue May 28 17:50:20 EDT 2002 | myu
Hi, Everybody! I'm looking for a High-Temperature Solder Paste / wire: "Pb93WROL140.71454";or "00Z890"; J-STD-006 Solder Alloys Sn05Pb93Ag02B Sn% Pb% Ag% Solid C Liq C Solid F Liq F 5.0 92.5 2.5 280 284 536 543 It should meet IPC/J-ST
Electronics Forum | Tue Jul 30 12:15:15 EDT 2002 | Rick Lathrop
Hi Dave, The paste applied to the board ends up on the tombstone. The pad has a thin covering of solder most of the time, this is why I think they call it a dewet. Occasionally the pad shows some areas of gold and very rarely are some pads not wet at
Electronics Forum | Wed Oct 02 18:18:58 EDT 2002 | davef
The steadfast rule of thumb is: In order to get reliable reflow, you need to be at or higher than [liquidus + 20�C] for about 5 to 10 seconds, rather than those old "60 seconds above 183�C" guideline. This provides for setting your peak based on the
Electronics Forum | Wed Oct 09 16:59:35 EDT 2002 | davef
Russ, as I told Eric the other day ... The steadfast rule of thumb is: In order to get reliable reflow, you need to be at or higher than [liquidus + 20�C] for about 5 to 10 seconds, rather than those old "60 seconds above 183�C" guideline. This prov
Electronics Forum | Thu Oct 31 16:13:46 EST 2002 | babe
If your processing with Nitrogen, tombstoning can be caused by your cooling rate. Go thru the solid/liquid phase of the solder slower..iN other words as you transition into or out of the liquidus pahse if 63/37 alloy 183C, ensure that your Delta are
Electronics Forum | Tue Dec 10 10:26:56 EST 2002 | davef
Questions are: * What is the current plating on the connector that is over the "plating of the leads is Nickel (99.9% purity)"? * What are the temperatures and durations at those temperatures that you read on these connector leads? * What solder allo
Electronics Forum | Tue Dec 10 19:30:49 EST 2002 | Vijay
Hi Dave, The peak temp on the leads is 216-218 Deg C and duration above MP (179 degC) is 55-60 sec. Alloy(solder paste) used 62 Sn,36 Pb 2Ag (Alpha WS 609 Ty 3 Water eash) This is a SMT connector wth Gulwing leads Gold plating on the PCB is 2-5 micr
Electronics Forum | Thu Dec 19 12:08:01 EST 2002 | davef
Facts!!! I got facts. Mechanical strength experiments of Sn43/Pb43/Bi14: �Microstructural And Mechanical Characterization Of 43/43/14 Tin/Lead/Bismuth�; J. Marshall, J. Calderon, J. Sees; Soldering And Surface Mount Technology; 10/91, p25-27 Look
Electronics Forum | Tue Jan 21 11:11:07 EST 2003 | slthomas
OK, so the issue is with the variability of the alloys on the soldering surfaces and the subsequent variability of reflow temps. Sounds reasonable (actually obvious, now that I think about it), especially on the component side. We only use HASL fin
Electronics Forum | Tue Apr 29 09:39:52 EDT 2003 | Adam
We are thinking of changing our solderbar supplier,due to a significant price increase from our current supplier.My question is, if the alloy is the the same, is it just a case of topping up the solderpot with the solderbars from our new supplier, as