Electronics Forum | Fri Sep 14 12:22:49 EDT 2012 | grauen06
The Alpha EF-9301 flux worked great! We went from ~4 solder issues per PCB to
Electronics Forum | Fri Mar 22 14:19:38 EDT 2019 | gregcr
Thank you ProcEng1 Nordson sent me a flux suggestion list: No Clean: 1. Kester Select 10 2. ALPHA EF-2210 3. AIM FX-16 Water Sol: KESTER 2331-ZX Nozzle Tinning: SUPERIOR #75
Electronics Forum | Tue May 09 14:49:57 EDT 2006 | Larry
Hey guys, Anybody having trouble with increased false contact issues in ICT after switching from lead to lead free? Our test guys keep trying to imply that the flux residues are a problem (we're using Alpha EF2202), but as the soldering process eng
Electronics Forum | Thu Dec 18 14:38:41 EST 2008 | easton
I think the BLT solder joints look very shiny for no-lead. We are getting very good top side solder with ours though. They look like this. - Gold Enig plating - Alpha EF-6100 Flux - SAC305 - Preheat topside temperatures at 110 to 120C
Electronics Forum | Fri Jul 29 16:20:57 EDT 2016 | davef
"ALPHA® EF-2210 is VOC-free, halide-free, rosin/resin-free, low solids no-clean flux which provides the highest activity of any VOC-free Bellcore SIR compliant flux for defect-free soldering. "[2016 Alpha Assembly Solutions] I assume that you're tal
Electronics Forum | Thu Nov 30 00:41:23 EST 2017 | abhilash4788
Dear All, I have OSP finsh pcb on my production, the pcb thickness is 1.5mm and the product is one sideded pcba. After reflow process, Is there any specific time frame defined for smt completed OSP finish pcba before going for wave soldering proce
Electronics Forum | Thu Mar 11 11:08:22 EST 2010 | geocep
I am using AIM Electropure SN63/Pb37 Solder, & AIM NC266-3 Flux; just like what ACE recommends. I have both Ultra High Pure T-Tanks and a Cryogenic Dewar Tank for Nitrogen, and neither seems to have improved the problem. I place a piece of tempered
Electronics Forum | Fri Jun 22 21:07:08 EDT 2012 | tank1266
I have had Selective issues such as yours on two very different Selective Solder Machines. I was able to eliminate these issues by using Alpha EF-9301 wave flux with any SAC305 solder. It's a more aggressive flux, but really made the difference. Anot
Electronics Forum | Fri Jul 29 06:16:19 EDT 2016 | dmsm123
We do have a commen problem with flux residues after the wave soldering process, even after using correct wave soldering profiles recommended by the flux supplier, The following flux type is being used Alpha EF 2210 VOC Fre Bellcore No Clean water Ba
Electronics Forum | Mon Jan 15 09:19:29 EST 2007 | tk380514
We use Alpha EF-2202 low-VOC No-Clean flux Selective wave soldering cassettes Bottom pre-heating wave soldering machine We have one component that will not solder properly: http://www.epcos.com/web/generator/Web/Sections/ProductCatalog/Capacitors/Ul