Electronics Forum | Tue Jul 27 10:22:09 EDT 2004 | Chris C
By looking at the solder balls they have not joined with the other particles that are alongside them. suggesting that they did'nt reflow. But they could very well be as you suggested, reflowed and ejacta from the process. We have been experiencing
Electronics Forum | Wed Jul 28 00:12:48 EDT 2004 | NTV
It would be uncontrolled reflow process. Solder paste smeared, outdate solder paste, contamination, and many else could lead to this issue. A longer time reflow window would help elimating it (make it max. of 60 seconds liquid time).
Electronics Forum | Wed Jul 28 00:12:52 EDT 2004 | NTV
It would be uncontrolled reflow process. Solder paste smeared, outdate solder paste, contamination, and many else could lead to this issue. A longer time reflow window would help elimating it (make it max. of 60 seconds liquid time).
Electronics Forum | Wed Jul 28 00:12:58 EDT 2004 | NTV
It would be uncontrolled reflow process. Solder paste smeared, outdate solder paste, contamination, and many else could lead to this issue. A longer time reflow window would help elimating it (make it max. of 60 seconds liquid time).
Electronics Forum | Wed Jul 28 00:13:21 EDT 2004 | NTV
It would be uncontrolled reflow process. Solder paste smeared, outdate solder paste, contamination, and many else could lead to this issue. A longer time reflow window would help elimating it (make it max. of 60 seconds liquid time).
Electronics Forum | Wed Jul 28 00:13:23 EDT 2004 | NTV
It would be uncontrolled reflow process. Solder paste smeared, outdate solder paste, contamination, and many else could lead to this issue. A longer time reflow window would help elimating it (make it max. of 60 seconds liquid time).
Electronics Forum | Mon Jul 26 14:54:44 EDT 2004 | Tim Walters
I was wondering if anyone has information on the market size for solder preforms, paste, wire, etc. If not, do you have any suggestions on where I might find this information?
Electronics Forum | Thu Jul 29 21:22:41 EDT 2004 | davef
Look here: http://www.mindbranch.com/listing/product/R1-1940.html We have no relationship, nor receive benefit from the company linked above.
Electronics Forum | Mon Jul 26 14:58:52 EDT 2004 | cisridn
I am new to the No-Clean Process. When preforming rework in a No-Clean Process, should the rework technician clean the excess flux used to change a component or place a component missing?
Electronics Forum | Tue Jul 27 04:42:36 EDT 2004 | Adam
Hi Does anyone know where I can purchase trolleys for the storage or IC's and other components that come in tubes and sticks ? Thanks in advance