Electronics Forum | Thu Dec 29 04:19:52 EST 2005 | lvqp72
We've run into a persistent QA error 99 on one of our Quad IVC's. Have checked upon all the obvious and found no bad components. Do appreciate any advice on this problem. Thanks.
Electronics Forum | Fri Dec 30 10:12:27 EST 2005 | Cmiller
Joseph, thank you for your comments. Can I ask what kind of flux you are using?
Electronics Forum | Sun Jan 01 21:02:54 EST 2006 | sumxp
Please elaborate more on hole fill issue.How difficult to optimise the process para?
Electronics Forum | Mon Jan 02 08:54:58 EST 2006 | aj
has anyone used or trialed the SACX from Alpha, from reportes and studies carried out it seems that its a go between SAC305 and SN100.
Electronics Forum | Wed Jan 04 17:06:20 EST 2006 | samir
All I can say about Alpha and their GOTT-DAMN website is THEY SUCK!! I refuse to register to view product literature... for that reason, Alpha Metals, you won't be looked at for my pb-free paste or bar solder evals.
Electronics Forum | Fri Jan 20 08:27:28 EST 2006 | Loco
Just wondering what the companies that are use SN100C are using for reflow (I guess SAC), and especially for handsoldering. Do SAC and SN100C mix? are there any studies proving this?
Electronics Forum | Fri Mar 03 13:44:36 EST 2006 | Jon Provost
We switched to Sn100C on 2 waves and kept one with SAC305. The SAC305 will be converted to SN100C as soon as the Aim rep. delivers it next week.
Electronics Forum | Fri Mar 31 15:49:51 EST 2006 | GS
Hi Marcus, by using SN100C have you seen any tearing phenomena like what shown on the link ? http://www.smartgroup.org/pdf/Defect01.pdf Tnks Regards.........GS
Electronics Forum | Thu Apr 06 17:42:59 EDT 2006 | GS
found this interesting comparison (SAC305 SN100C) http://www.nihonsuperior.co.jp/english/data/pdf/nse2_1.pdf Regards..........GS
Electronics Forum | Mon Apr 10 13:10:06 EDT 2006 | Marcus
No I have seen Zero hot tears. Thats with water soluble or No-Clean. We have built over 10,000 boards.