Electronics Forum | Thu Jul 26 14:06:46 EDT 2001 | johnmaetta
That's a good question. On some of the assemblies that our engineers test, appear to have been reworked in these suspect locations. I have requested rework data from our CM by providing them with assembly and serial numbers. Their data shows that th
Electronics Forum | Sat Jul 28 10:51:38 EDT 2001 | nifhail
I'm curious over what would happen if we continue to use the WS paste when dealing with uBGA. Definitely the cured flux under uBGA package couldn't be cleaned/reached and as I understand correctly they are corrosive. if that so, how long do you guys
Electronics Forum | Tue Jul 24 03:26:45 EDT 2001 | winnifred
Dr. Lee, For lead-free wave soldering, we are recommended to use SnCu0.7, why not 0.8 or more ?? Since SnCu0.7 has eutectic melting point at 227 deg C, does it mean with more Cu or less Cu, the melting point will be higher ?? Also, in lead solderin
Electronics Forum | Thu Jul 26 02:48:07 EDT 2001 | mugen
Ahem..... in my humble opinion, (whether it matters or not, depends on whether you are n'sync with me) I would be as so bold, to declare, the SMTnet server, keeps "handing" occasionally, during transmit of our respective thread postings.... sometime
Electronics Forum | Wed Jul 25 13:03:52 EDT 2001 | davef
I just finished cleaning-up [I hope] a SCAM32 virus from my computer. I opened an attachment to an email received through SMTnet asking for assistance. The file had a ".doc.pif" extnsion. The virus is sending emails to my address book. Do not ope
Electronics Forum | Wed Jul 25 15:00:07 EDT 2001 | akruppa
Yes, this has been a problem for a number of users. The virus is a worm distributed via e-mail. The message it sends reads: "Hi! How are you? I send you this file in order to have your advice See you later. Thanks" Opening the attachment will
Electronics Forum | Wed Jul 25 16:36:10 EDT 2001 | akruppa
We have found and quarantined a number of attachments received in site user Web Mail accounts containing the W32.Sircam.worm. This may cause a file not found error for some users, when attempting to download or open the attachments. We will periodi
Electronics Forum | Thu Jul 26 09:22:20 EDT 2001 | nwyatt
We are currently testing 0201s. We are using T3 paste, and it is working fine. You will need specialized feeders, test components, and test boards. Also depends what machines you are using - some are not capable of placing 0201 components. My s
Electronics Forum | Wed Aug 01 23:47:38 EDT 2001 | nifhail
Hi Dave G, What is the estimated Price for the complete database. Don't have to be accurate. I was trying to get our IT to help in designing the basic database for feeders' tracking but, now they hv asked me to write ROI, I have a real bad headache
Electronics Forum | Fri Jul 27 13:16:03 EDT 2001 | cjrjmj
I am looking at the Pump application for several bottom side applications we have. They are heavy in through hole radial and dip content. The initial testing of the stencil was very good, but I am concerned with inspection of the glue. We do a sampli