Electronics Forum | Tue May 02 14:38:06 EDT 2006 | bhall
Currently I am using a water soluble solder paste and no clean wire solder. For awhile now I have been pushing to switch to no clean across the board. Can anyone give me an idea of how this will effect production? Switching to no clean will allow m
Electronics Forum | Thu May 04 08:49:38 EDT 2006 | russ
Please read your manual, I am sure that it will address proper maintenance of your oven ducting and flux build up. The MFGR will also be able to specifically address your problem and let you know if any upgrades are available. Flux collection filter
Electronics Forum | Wed May 10 00:56:39 EDT 2006 | serg
Date: May 09, 2006 03:29 AM Author: Slaine Subject: core of a transformer what specification do you need, whats the working temp, do you need it to be ? emmerson and cumming do a range of epoxies that might be of use? Yes I search glue for
Electronics Forum | Tue May 16 11:58:27 EDT 2006 | jsloot
What is the best or ideal cleaning method for wave solder pallets? I have been using iso prop and am not sure if this is the cause for having brittle wall material. I wouldn't think alcohol would degrade the durastone material. Most of my pallets hav
Electronics Forum | Tue May 23 09:36:11 EDT 2006 | Steve
Not being funny here but I understand exactly what you are saying and sounds exactly the same as we experienced. Seriously try a different paste. Give Tamura a ring and I am sure they will give you a sample. I don't have the exact part code but they
Electronics Forum | Mon May 22 23:29:11 EDT 2006 | fordf1502004
I am currently using a sanyo V850 machine. We are haveing problems with the upline and downline communication from the sanyo to any other conveyor. The conveyors we have on hand all use smemma, and the sanyo has an adapter box that connects to the sm
Electronics Forum | Thu Jun 22 04:35:19 EDT 2006 | emeto
Hi netellink, I am not familiar with suzuki machines, but it usually works that way. There is a sign on the nozzle(it could be dots or lines...)and a recognition file for it. So you have to check: - if the sign the machine is looking for is damaged
Electronics Forum | Tue Jun 06 10:48:47 EDT 2006 | jsloot
Perhaps there is someone who can answer this question. If a 1k 1% 0805 ohm resistor is missing a corner is it still going to read 1K ohm? Or, if it has an extra bit of material is it going to read more than 1k ohm? I am guessing that when chip reisis
Electronics Forum | Fri Jun 23 09:02:17 EDT 2006 | paulinct
Glad to hear it is running good for you. I have my new wave solder machine in house.(hooking it up next week). I am debating between Sn100 and Cobalt 995 (metallic resources). Does anybody have an experience with the Cobalt. Or a reason not to go wit
Electronics Forum | Fri Jun 09 08:20:56 EDT 2006 | kehoem@bellsouth.net
We have a board calling out for 50 micro-inches of nickel over 30 micro-inches of gold. This is a solid gold board on Rogers material. ENIG cannot be deposited that thick right? Electroplated gold (we thought) was usually 35-50 micro-inches and was