Electronics Forum | Fri Dec 05 11:13:06 EST 2008 | dilogic
We are running an older GSM1 machine (sw.runs on OS/2) and I would appreciate any hints which vision algorithm to use for best results with QFN and similar parts. One of the ULC's is 2.6mil/pixel. - Dejan
Electronics Forum | Fri Dec 05 12:26:38 EST 2008 | 4balisong
After hand soldering I am getting solder flags on my boards (see attachments). Any one have an idea on how to get rid of these flags or are those acceptable?
Electronics Forum | Tue Dec 09 15:30:16 EST 2008 | markhoch
your best bet might be to try contacting some of the industry leaders in Aqueous Cleaning Equipment. Zestron America www.zestronusa.com Speedline Electrovert http://www.speedlinetechnologies.com/electrovert/aquastorm.aspx I am not affiliated in
Electronics Forum | Mon Dec 15 05:41:27 EST 2008 | leeg
Does anyone know of any UK based company that supplies spares/blades for the above machine?
Electronics Forum | Fri Dec 19 11:57:29 EST 2008 | robinj
Experts, Any advise on Hot Bar Soldering.I'm relatively new to this process.What are the pros and cons as opposed to using connector?
Electronics Forum | Mon Jan 12 02:56:42 EST 2009 | sachu_70
Hi Bill, You should try pre-baking any such old devices prior to using on SMT Reflow. Refering to MSL-type3 guidelines could help in your case.
Electronics Forum | Mon Jan 05 03:12:54 EST 2009 | lococost
If you can use a IR desoldering station, you could try covering the second BGA with aluminum tape. The tape shouldnt touch the second BGA, it should form a 'roof'over it that reflects the IR waves.
Electronics Forum | Mon Jan 12 23:25:27 EST 2009 | sachu_70
Did you try explaining the problem to your machine manufacturer for direct assistance? Perhaps your machine brochure would indicate a 24hrs helpline service, or any contact no.
Electronics Forum | Tue Jan 06 18:06:05 EST 2009 | aj
Hi all, I am currently trialling a solder paste which contains Bismuth. It is leadfree and reflows at 138 degrees C. I would appreciate any pros/cons? aj...
Electronics Forum | Fri Jan 16 06:53:33 EST 2009 | stevewilde
I am using Humiseal 1B31 conformal coating and xylene mix on a PVA coating machine. Bubbles are appearing between the pins of LCCs mainly and bubbling is worse when put through the IR oven. Does anyone have any suggestions or tips to elliminate this