Electronics Forum | Sat Jan 23 16:07:20 EST 1999 | Steve Gregory
| hi, | i am working towards developing a no-clean process for a customer at contract manufacturing facility. the assemblies have gold fingers on them. these are masked to prevent from any damage to them during reflow soldering. the earlier proces
Electronics Forum | Tue Jan 05 18:07:53 EST 1999 | Dave F
| I am looking for information regarding post wave soldering of stranded wires into a circuit board using OA core wire solder. We do a final pass thru the cleaner after the hand soldering but I'm concerned about any OA flux residue that may have wic
Electronics Forum | Wed Dec 23 03:33:14 EST 1998 | Charles Stringer
Can anyone recommend a solder stop that can be applied by our PCB supplier. Our current material form Tamura Kaken is causing problems. The material should be capable of withstanding 1 Surface mount IR reflow cycle and 1 wave solder cycle. We need t
Electronics Forum | Fri Aug 21 14:29:37 EDT 1998 | Earl Moon
| HASL: (hot air solder leveling) is a process used to cover the Cu. Either Sn/Pb is used or Ni/Au or some other combo. In one case you create a land pad and in the other (with resin)you cover the Cu so that you only have a "trace." Is that correct s
Electronics Forum | Thu Jul 23 11:39:16 EDT 1998 | Russ Miculich
Are you using a HASL board or an organic protection on the pads? This will help determine as to whether paste is necessary or just a very active/tacky flux should be used. Tight process control will also help in the reflow oven. Many users don't wan
Electronics Forum | Mon Jul 06 17:42:49 EDT 1998 | Bruce Houghton
| I'm having a problem getting good reflow on gold sufaced boards. The profile looks good and I have adjusted it both hotter and colder and adjusted the various times ( soak, reflow ) to no avail. What realy gets me Is that a month ago we built some
Electronics Forum | Thu Jun 18 10:57:28 EDT 1998 | Mike Moninger
| We offer an upgrade service for notebooks with 486 SX/DX CPUs up to 586-133 MHz using the AMD 5x86-133 MHz CPU in the PQFP package. We are pretty succesful with this service and until today we did more than 1000 notebook upgrades this way. | Now,
Electronics Forum | Sat Apr 25 19:40:01 EDT 1998 | Stan Traxler
| We have to mount our SMD devices 0.1 to 0.4 mm off the pcb | PCb substrate to compensate for thermal stressing in a | Space enviroment. Has any one any ideas or contacts for | dissolvable pads. this only applies to leadless components We have appl
Electronics Forum | Wed Mar 18 22:43:07 EST 1998 | Scott McKee
| | Is there anyone out there required by their customer to clean the finget tab contacts even after using noclean paste? We have been asked to clean even though we don't have any flux residue on the contacts. Any ideas? | | Mike | | Yes and often
Electronics Forum | Thu Mar 26 23:17:04 EST 1998 | Marty Fox
| | | Is there anyone out there required by their customer to clean the finget tab contacts even after using noclean paste? We have been asked to clean even though we don't have any flux residue on the contacts. Any ideas? | | | Mike | | | | Yes a