Electronics Forum | Thu Oct 02 17:00:44 EDT 2008 | davef
Is that accurate? If so, what are your aspect & area ratios? [Similar to the JerryS comment above.] * You say, � � and the average height is very high: nearly 200 pct.� => Our troop can make paste that height too. They snap the stencil-off a fast as
Electronics Forum | Mon Oct 15 10:51:49 EDT 2001 | davef
On over printing, the general issues are: * Paste deposits being so large that when reflowing, collapse onto many, rather than a single solder mass. * Paste expanding during heating and being close to other solder deposits and bridging [as you say].
Electronics Forum | Mon Nov 15 12:13:41 EST 1999 | Dave F
Steve: There are guidelines for determining if your aperture has the correct proportions to the foil thickness. Maybe that�s what you�re looking for: 1 Aspect ratio = aperture width/foil thickness Chemically etched SB GT 1.5 Laser cut SB GT 1.2
Electronics Forum | Mon Nov 15 12:09:55 EST 1999 | Dave F
Steve: Continuing with Dan�s thinking, generally, "poor release" (paste hanging-up in the stencil holes) could have three main (or combination of) causes: 1 Equipment: Stencil is too thick. Specifically, your 0.006 should be OK, providing you don�
Electronics Forum | Wed Sep 18 12:31:16 EDT 2002 | dragonslayr
My suggestion is to conduct a Design For Manufacturing (DFM)study on the assembly in question. Pay particular attention to the pad sizes, component lead dimensions and satisfy yourself that those two factors are correct. Given that pads match compone