Hi All, I have some question about expired solder paste. What would be some of the effects regarding assembly quality. Is there any changes in flux composition toward the end of shelf life? Thanks in advance for any replies.
Electronics Forum | Fri Apr 04 01:39:21 EDT 2008 | slthomas
All of what Dave says is spot on. I suspect that the most likely corresponding defects on your assemblies would be poor wetting and insufficient solder.
Electronics Forum | Thu Apr 10 16:02:04 EDT 2008 | brulal1
Hi,we are looking to use Press fit connector on our PCB assemblies. Did anyone out there have any issue with press fit connector? Thank Bruno
Electronics Forum | Wed Apr 23 17:28:46 EDT 2008 | davef
The need to prebake boards to remove moisture from the board [to prevent voiding] prior to wave soldering is driven by the thickness of through hole plating. * 1 thou [25um] or greater requires no prebaking * LT 1 thou [25um] requires prebaking
Electronics Forum | Tue Apr 29 02:08:21 EDT 2008 | sin4d
Hi, I am also facing the same probelm. I assembly a substrate with a thickness of 0.30mm and the board warp after reflow. If I bake the substrate at 125 Deg C for 2 hours will it help to solve this problem? Thanks
Electronics Forum | Thu May 01 13:58:31 EDT 2008 | mmjm_1099
In our house we have had some of our BGA's reballed because it was a lead-free part and wanted to place on a leaded assembly. Hope this helps.
Electronics Forum | Thu May 01 10:31:26 EDT 2008 | cdsullivan
Good Morning, We are seeing an increased number of our customers that specify a Pb-Free BGA when the rest of the board assembly is SnPb. Of course when we reflow at the SnPb profiles, we don't always get a properly collapsed BGA. So we end up rewor
Electronics Forum | Thu May 08 15:41:07 EDT 2008 | shrek
I once took a pair of binoculars and stared at a wave solder for over an hour.