My company is currently using point source soldering of SMT components. We have seen some problems due to improper soldering and are looking to switch to a reflow oven/hotplate assembly. Our PCB's range in size but are no larger than 5"x5" and we as
Electronics Forum | Sun May 28 19:02:11 EDT 2006 | grantp
Hi, One thing, getting back to the original topic, is you might want to panelize these boards as much as possible, as you don't have too many components, but you have some good volume. So the machine changeover time is going to be an issue. Althoug
Electronics Forum | Fri Jun 09 15:46:34 EDT 2006 | samir
I say: �Wave flux needs to be heated to certain activation temps which won't be repeatedly achieved with a manual soldering process. Plus, you won't burn off any residual activator as you would if the board were immersed in a solder bath.� Muse say
Electronics Forum | Tue Jun 13 04:46:15 EDT 2006 | AR
Has anybody else noticed a problem with Assembl�on's mechanical 12 mm feeders, with 4 mm pitch? We are experiencing grave pickup problems with a MELF diode packed this way and fed with this type of feeder. If I attach a hefty weight to the blister ta
Electronics Forum | Tue Jul 18 16:40:09 EDT 2006 | dphilbrick
We have a system where when we set up the line to run a job before the first part is placed an auditor verifies we have all the correct parts loaded on the machines in thier correct locations. We then run a first article. The board is inspected to in
Electronics Forum | Sat Aug 12 20:47:50 EDT 2006 | Efren
Hi Guys, A few months ago I posted a question about a New Assembly Line, and It was great the answers I received. Now I would like to have an additional advise, to complete the requirements of my financial. We expect to install approximately 6 Pick
Electronics Forum | Fri Nov 03 11:06:13 EST 2006 | rgduval
The process that burnt the tips up yesterday was hand soldering/touch up of lead-free assemblies. Not even assembly, but just touching up boards that we've soldered on a solder pot...which will lead to another question. We're using SAC 305 WS482 3
Electronics Forum | Tue Nov 07 18:18:03 EST 2006 | Andrea
I am wondering how to move from hand soldering our ceramic caps to doing a reflow type process. The reason for the change is too many cracked ceramic caps. I have asked our vendors to assemble our boards via reflow but because of our hardware (swaged
Electronics Forum | Thu Nov 30 12:12:14 EST 2006 | pbarton
I am in the process of characterising a new vapour phase reflow system and am interested to learn if anyone out there has ever come across time/temperature datalogging equipment capable of being run through the entire process (including vacuum) along
Electronics Forum | Thu Dec 07 13:51:59 EST 2006 | ganoi
I need advices as to how a gap between the bottom of an LED (1209-package) and the PCB can be controlled on a small rigid-flex PCBA? The problem that we experience is due to tight tolerance in the design of our molded housing in which this PCBA is as