Electronics Forum: au wire bonding (Page 1 of 23)

Au Wire bonding failure

Electronics Forum | Wed Dec 14 12:34:56 EST 2016 | cy4223111

Hi all, Recently, we are trying to do wire bonding between a 75 * 75 um pad on a chip and substrate with 150 um height difference, but when completing wire bonding and the wire bonds on pad and substrate, the pad will get out of the chip easily

Au Wire bonding failure

Electronics Forum | Wed Dec 14 20:17:48 EST 2016 | davef

As I understand, you are wire bond gold wire to gold pad, where the substrate has good bond strength, but the die does not. If bond quality is good, and then drops off rapidly, then it's probably something to do with contamination within the system

Au Wire bonding failure

Electronics Forum | Fri Dec 16 13:37:52 EST 2016 | edhare

Hi all, > > Recently, we are trying to do > wire bonding between a 75 * 75 um pad on a chip > and substrate with 150 um height difference, but > when completing wire bonding and the wire bonds > on pad and substrate, the pad will get out of

clean rooms/ wire bonding

Electronics Forum | Mon Mar 07 15:41:50 EST 2005 | John M

Is anyone aware of standards which would identify the clean room requirements for the wire bonding process ?

gold wire bonding

Electronics Forum | Wed Dec 28 03:33:31 EST 2005 | sparrow

I would like to know if ENIG is widely used for the thermosonic gold wire bonding or this application is an exotic one. And I also wold like to talk to someone who uses printed circuits with ENIG finish for such an application. I do not quite underst

gold wire bonding

Electronics Forum | Wed Dec 28 21:18:12 EST 2005 | davef

You don't TS bond gold wire to nickel [of ENIG] for the same reason that you don't TS bond gold wire to hard gold. [Nickel or maybe cobalt is used to harden soft gold.] Together nickel and gold produce unreliable bonds. Look here: * http://www.smta.

clean rooms/ wire bonding

Electronics Forum | Mon Mar 07 21:37:42 EST 2005 | ABHI

It depends on your product requirements. I have seen aluminium wire bonding operations in as high as class 100K clean rooms. These are the assembly areas for calculators. The best is class 10K clean room for wire bonding. You can go upto fine pitch w

gold wire bonding

Electronics Forum | Tue Dec 27 10:00:19 EST 2005 | sparrow

Hello, does anybody have experience in thermosonic gold wire bonding to electroless nickel/immersion gold?? regards, Sergey

gold wire bonding

Electronics Forum | Thu Dec 29 03:57:16 EST 2005 | sparrow

Hello Chris, To be honest, it's hard to believe you could not bond to ENIG at all. Yes, the gold layer is thin and hard, but it just narrows the process window and does not make the bonding impossible. I say this, because we have been using TS gold w

Aluminum wire bonding

Electronics Forum | Sun May 26 10:21:46 EDT 2002 | V.RAMANAND KINI

We buy PCBs for aluminium wire bonding. Our PCBs have 0.25 mm square pads for bonding and 0.10 or 0.15 mm gap between circuit traces/tracks. We do not have any problem. Our vendor gives 9 microns of Nickel and 0.03 microns of gold.

  1 2 3 4 5 6 7 8 9 10 Next

au wire bonding searches for Companies, Equipment, Machines, Suppliers & Information

SMTAI 2024 - SMTA International

Component Placement 101 Training Course
Electronics Equipment Consignment

High Precision Fluid Dispensers
Fluid Dispensing, Staking, TIM, Solder Paste

Software programs for SMT placement and AOI Inspection machines from CAD or Gerber.
SMT feeders

World's Best Reflow Oven Customizable for Unique Applications
design with ease with Win Source obselete parts and supplies

Internet marketing services for manufacturing companies