Electronics Forum | Mon Oct 19 15:43:37 EDT 2009 | dilogic
We have a problem with QFN IC's with NiPdAu plated pads. Our ULC's don't see the pads due to the almost ideal reflection. Vision sees the pads almost black. As we don't have OAL-cameras (which can help in this case, I assume), I am thinking of back-l
Electronics Forum | Tue Oct 20 17:30:15 EDT 2009 | rodrigo
Hi all, We use the IMF converter (and a floppy disk) to move programs to and from the MCS30. The only way to get to the command line in the MCS30 is to reboot and do the ctrl+shift+_ ketpresses. I wanted to try to add an entry to the Fuji User inter
Electronics Forum | Thu Dec 17 18:08:41 EST 2009 | lynn_norman
Back in a former life, we had 3 products that were PCBs bonded to aluminum boards. We used a PSA from 3M to bond the board to the aluminum. Polymers are almost invisible in x-ray, but ultrasound worked quite well. You should try CSAM. Don't know
Electronics Forum | Fri Feb 26 17:16:24 EST 2010 | jlawson
If you have trouble also you can check out Valors vPlan, i have it running Yamaha YV100Xxg machines - they support Assembleon versions too. Can generate VIOS files from ALtium Input - either CAD DB files or ODB++ as Altium Designer supports this now.
Electronics Forum | Fri Mar 19 12:53:35 EDT 2010 | pcbrookie
Hello everyone. I'm looking for some general information on reel counters. We are trying to tighten our inventory counts, and rather than estimate a reel we're looking into getting an accurate count via a reel counter. So first, I'm wondering what
Electronics Forum | Tue May 25 12:17:44 EDT 2010 | markhoch
Dang, you're picky. Try buying your operators mittens, and then tell them that your company has discovered that mittens generate less ESD so they're making them mandatory now. Then...after a few hours, bring them their gloves back and tell them that
Electronics Forum | Tue Jun 22 00:09:14 EDT 2010 | leadthree
You should do some testing what temp you really get. Solder will melt 260~300ºC. Back to the initial question, CEM-3 is a bit harder to buy and has not many varieties. Go for FR4, you can go for a higher Tg then the common 130ºC. There is also 140,
Electronics Forum | Wed May 26 13:17:32 EDT 2010 | emrtech
FYI we also found a set of centering jaws that were up for sale at http://www.mybidpage.com these were also modified and made of stainless steel. the guy a bought the jaws from also said, he would be posting more up for sale after getting them back f
Electronics Forum | Thu Jun 17 10:22:51 EDT 2010 | floydf
Last July I posted a query about reflowing leaded paste to gold plated boards, I wasn't getting a good reflow. The answer that seemed to work was dwelling the board at reflow for the maximum recommended amount of time. Would anyone have an opinion on
Electronics Forum | Thu Jul 01 15:12:16 EDT 2010 | siddharth
Thanks to all for their inputs. @Hexielectronics, I am now trying to assemble the board by attaching it to a frame and removing the frame while waving it. I plan to put the boards back on the frame after the board cools down. Could you explain more