Electronics Forum | Fri Jun 04 03:03:52 EDT 1999 | Scott B
| I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | We've been getting a rash of defects that we call in this company, "insufficient solder in VIA hole." The
Electronics Forum | Fri Jun 04 15:04:16 EDT 1999 | Earl Moon
| I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | We've been getting a rash of defects that we call in this company, "insufficient solder in VIA hole." The
Electronics Forum | Sat May 29 16:56:26 EDT 1999 | Jeff Sanchez
| | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a double-
Electronics Forum | Sun May 30 10:15:34 EDT 1999 | Vic Lau
| | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a dou
Electronics Forum | Wed May 26 10:00:03 EDT 1999 | David Scott
| | | | | | | | | | | | Any suggestions on how to maintain Adhesive dispensing nozzles??? They seem to plug up over night and it is starting to get on my nerves. We have tried leaving the nozzles in the machine, removing them and soaking in alcoh
Electronics Forum | Fri Aug 31 08:45:33 EDT 2001 | 0704494250
Hey peoples, We are working with the dairy > industry out here and they asked us to start > reworking all there boards for them. Of course we > said yes, hehe. Only we didn't know what them > farmers coated them boards with. It turned out to
Electronics Forum | Mon May 24 09:52:06 EDT 1999 | john thorup
| | | Has anyone had any experience or data using vibration during the reflow process. | | | We introduced a vibration device attached to the fixed rail on a Vitronics reflow oven. The reason was to prevent skewing on large PLCC devices. The process
Electronics Forum | Wed Apr 28 11:47:34 EDT 1999 | Frank Boyko
| | We use Immersion Gold (AuNi) for our 20 mil pitch and BGA boards. | | Lately, we have been having solderability problems with boards with this surface from some of our suppliers. | | | | We are considering trying boards with White Tin solderable
Electronics Forum | Tue Apr 13 18:39:24 EDT 1999 | Tom B
| | Netters, | | | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | | | 1. Kester 293 no clean | | 2. 2.1 C/s for 30s to 150 C | | 3. .5 - .7 C/s f
Electronics Forum | Tue Apr 13 23:08:56 EDT 1999 | Jeff Sanchez
| | | Netters, | | | | | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | | | | | 1. Kester 293 no clean | | | 2. 2.1 C/s for 30s to 150 C | | | 3.