Electronics Forum | Thu Sep 09 03:57:45 EDT 2004 | svi
Hello, We used FujiCAM to prepare FCM programs but now we're thinking to change it to an other software. We have some FCM and some (more) FUJI machines also. We used FujiCAM to controll and proram the lines but we changed it to Fuji FlexA. Microsof
Electronics Forum | Fri Sep 24 22:43:07 EDT 2004 | FengAng
Hi Rob, We use the most advanced equipments in front end, but the back end we always use manual assembly, including display, LCD, casing. It's all because we should balance the cost & efficiency. I think if you are the boss, you will also do thing
Electronics Forum | Mon Oct 25 17:50:46 EDT 2004 | Mike
I work for a PCB Manufacture and I am looking for info on BGA Pull test or strenght test. I have a CM that is experiencing bga's with some weak joints. they are telling me that when they do their pull test the joints are breaking at the nickel inste
Electronics Forum | Wed May 04 09:37:08 EDT 2005 | MikeaJ
I would not recommend trying to cram or mix and match multiple images on a stencil. Especially if you are a contract house, and your clients don't understand why sending one board seperate from a panel of four is a pain in the face. However, I have h
Electronics Forum | Wed Jun 22 09:12:57 EDT 2005 | bsudak
Our manufacturing site has been struggling with soldering Alloy 42 TSOPs. Currently, we have to hand solder in one of our applications. Here are the particulars. Component: 54 leads, Sn plated, 400microinches +/-200. Process: Eutectic 63/37 Sn/Pb
Electronics Forum | Wed Jul 06 13:06:22 EDT 2005 | patrickbruneel
Dave, Great to see you more involved in the lead-free. I assume the tests you have done were in lab environment, would it be possible to explain how you measured the area reduction (loss of weight or reduction of diameter/thickness) and how did you
Electronics Forum | Wed Sep 07 16:53:15 EDT 2005 | GS
Contact Cookson Electronic, they can support you with OSP solutions (ENTEK---) new formulations for Lead Free apllication. Regards GS --------- from a 2003 Cookson presentation: Objective Although Existing ENTEK� PLUS CU106A technology is suc
Electronics Forum | Tue Jan 31 14:23:39 EST 2006 | samir
Chunks, For our lead-free eval, we had the same problem with "charred looking" solder paste up the component termination of one of the smaller discretes, coupled with excessive solder balling...this smaller part did see peak temps in the 240 range -
Electronics Forum | Fri Mar 24 22:03:23 EST 2006 | mika
Hi all, Is there anybody out there who have some experience of Valor Trilogy 5000 in respect of programming/line balancing SMT-lines consisting of Fuji CP6-4's and UIC-GSM's? Our company is seriously thinking about to go for UniCam and their solution
Electronics Forum | Sun May 21 19:14:53 EDT 2006 | grantp
Hi, I agree, and normally we would not act like this to a real person, but this guy is a joke, and it was funny to read the replies to it, and reply. Guru is never going to be part of this forum, because he's just some weird guy who's too arrogant