Electronics Forum | Thu Mar 05 07:49:00 EST 1998 | Steve Gregory
Hi Ron, Your question really opens up a "Pandora's box", but when you say you're not able to print perfectly, what is it exactly that you mean? Is the print lacking volume? Is it mis-registered? Are you bridging? Also, what printers have you used? Do
Electronics Forum | Fri Aug 17 08:37:47 EDT 2001 | jbieber
Gregory, I think that the profile is too radical, i.e. zone 6 to zone 7 temperatures are too far apart. I would guess that the solderjoints have not all reached 183C in zone 6 which is why the uBGA's do not have a symmetrical ball collapse. You may
Electronics Forum | Mon Sep 24 17:38:18 EDT 2001 | mparker
First question - do you have a rework station? If so, are you experiencing the same type of failures there? I have successfully used no-clean on uBGA's in the past. 6 mil solder bumps, 10 mil spacing. 88 sites. Are you reusing previously soldered uB
Electronics Forum | Fri Jun 14 14:25:05 EDT 2002 | davef
Good job clarifying things. So, your MELF are just rolling off the pads. So much for the rocket scientist that talked you into those �V� shaped apertures, eh? [Or taking it the other way: Wow, just think how bad it would be if they weren�t worki
Electronics Forum | Thu Aug 01 13:04:57 EDT 2002 | gdstanton
Its interesting. It appears I'm getting conflicting feeback from Indium. This says its not a problem... http://indium.custhelp.com/cgi-bin/indium.cfg/php/enduser/std_adp.php?p_sid=kTDKGClg&p_lva=&p_faqid=355&p_created=1014734692&p_sp=cF9ncmlkc29
Electronics Forum | Mon Jun 21 11:14:25 EDT 2004 | exmaintenanceleader
Dear Kanwaljit Singh, my opinion is following: 1)solderpaste type is ok - usual (alpha-metals has this problem inside the paste paste- holder problem) - what do the operator when production change -clean well the stencil holes!! no visible rest on
Electronics Forum | Wed Sep 15 14:06:40 EDT 2004 | frankR.
Hi Rick, Last year I've test about 15 different solder paste. To procede, I've started with different tests listed in different brochure including IPC. At the biginning, I had 15 different tests to do and at the end ( for the last 7 product ) I've
Electronics Forum | Fri Jan 21 05:20:06 EST 2005 | Rob
Find out your maximum feeder loading (number of slots taken up, not number of feeders - 8mm, 16mm, 44mm, waffle packs tubes etc), and your likely long term max feeder loading (ie what is in the pipeline, or could be). Next find out your required run
Electronics Forum | Sun Mar 12 01:58:44 EST 2006 | grantp
Hi, We have been soldering lead free BGA's onto products with lead based paste, and we have had no increase in defects at all. We have used a standard lead paste profile, so we are not altering the temps anything from what's recommended by the paste
Electronics Forum | Tue May 23 21:14:22 EDT 2006 | davef
First, where the temperatures that aare mentioned in the original post measured? Second, it sounds like the PdAg component terminations are not seeing enough heat [your soldering iron touch-up proves this]. Your 232*C peak is the absolute minimum s