Electronics Forum | Wed Jan 27 09:00:56 EST 1999 | Chris Fontaine
| | I have boards coated with Humiseal 1B73. At a late point mfg. site we need to remove a series of 0603 resistors for optioning purposes. I have been trying to determine the fastest, easiest way to re-coat the pads after removal. Drying time of the
Electronics Forum | Fri Oct 16 13:11:49 EDT 1998 | Steve A
The Kyzen product was brought to my attention from a chemist at Kester solders when I asked him what could remove no clean residue from a PCB that had been built weeks earlier. We soaked it in the Kyzen for 8 minutes and ran the board through the aq
Electronics Forum | Tue Oct 06 15:41:14 EDT 1998 | Mike C
| | Does sombbody know what DPM rate a good and reliable SMT assembly line (incl. solder paste print, assembly and feflow soldering) has? | | DPM is Defects per million, usually measured on components. We run a process consisting of small to medium b
Electronics Forum | Mon Apr 06 12:32:20 EDT 1998 | Roxanne Picou
March 31, 1998-Austin, TX --- Austin American Technology announces a new Pre-Wash feature for the Mega� II to operate in conjunction with AAT's patented closed-loop regenerative cleaning process. This feature allows for an optional dual chemistry
Electronics Forum | Wed Aug 15 16:04:23 EDT 2001 | davef
First, responding to your question � Several things on copper dissolution in solder are: * A 50um copper wire will dissolve in 60Sn / 40Pb solder at: - 200�C solder in 55 seconds; - 250�C solder in 20 seconds; - 300�C solder in 5 seconds; - 350�C so
Electronics Forum | Mon Sep 24 17:38:18 EDT 2001 | mparker
First question - do you have a rework station? If so, are you experiencing the same type of failures there? I have successfully used no-clean on uBGA's in the past. 6 mil solder bumps, 10 mil spacing. 88 sites. Are you reusing previously soldered uB
Electronics Forum | Sun Aug 18 06:23:34 EDT 2002 | bentzen
Hi Ken. It's always fun and a good exercise to debat on a interesting subject like this. I can see at your response that I have to clarify some of the issues. Yes, the placement machine should be the line bottleneck. And in a line with more placem
Electronics Forum | Wed Feb 26 23:59:48 EST 2003 | Mike Konrad
Grant, No-Clean paste + IPA = White Residue! #1: Stop using IPA #2: Switch to either a solvent-based de-fluxing chemical or an aqueous-based de-fluxing chemical. If you are using an ultrasonic cleaner for your boards as stated, do not use sapon
Electronics Forum | Wed May 28 06:44:15 EDT 2003 | iman
Mario, Hi, basic point about all quality systems, is the cost justified? Traceability is just one aspect coverage in the quality system. As a pointer, is your diploma project research might focus and narrow down into tracability in high-end product
Electronics Forum | Wed Sep 10 11:57:14 EDT 2003 | Mike Konrad
First, you must determine a few things: 1. What specific de-fluxing chemical are you going to use? Basic required determinations include the chemical�s pH, is it a VOC (if so, what is its VOC content), what concentration is the chemical used in (1