Electronics Forum | Mon Nov 06 10:29:28 EST 2000 | Dean Stadem
All of the replies have merit. Here is another one. Because the cause of the tombstoning is wetting forces that are imbalanced, and one end wets faster or more readily than the other, the 0402 lifts up on that end easily because of its low mass. Incr
Electronics Forum | Thu Feb 17 14:10:37 EST 2000 | C.K.
I'd have to agree with JAX here. This forum is intended to be a "Technical Bulletin / Newsgroup" and nothing else. Truthfully, these posts of the "old-timers" announcing their departures is getting..well.....OLD. I hate to see the Old-timers leave
Electronics Forum | Wed Feb 21 18:07:00 EST 2001 | billschreiber
Hi Ramon, The obvious answer you might expect to here from me is that you could probably reduce your misprint problem if you had a good stencil cleaning process. Please see my response to the question by MarkT on �Cleaning Materials� because it i
Electronics Forum | Tue Dec 14 17:02:04 EST 1999 | John Thorup
Hello Kris If you do have and OSP coating I'd say Curtis has nailed it. But you seem to have references to gold. Does this board have a standard nickle/gold finish. If so what sort of "solder on gold" problems were you having? Reading between the
Electronics Forum | Thu May 20 22:42:19 EDT 1999 | Dave F
| hi everybody, | We've been doing some studies on assembly of CSPs. We assembled these packages on micrivia-in-pad patterns. These are 15/13.5/11 mil pads with 6 mil design microvia, using photo/laser/plasma tech. We are seeing voids, as big as the
Electronics Forum | Thu Apr 08 13:24:36 EDT 1999 | ADRIANO FERNANDES
| | I am getting ready to purchase a spray fluxing system for a no-clean process. I have narrowed it down to the Nordson or Dover system. Does anyone have any experience with either. If so can you relate with me. I am a little leary of the Nordso
Electronics Forum | Tue Mar 16 14:05:04 EST 1999 | Steve Skinner
| Does anyone have any recommendations on spray fluxers? Are there major differences between the high priced ultrasonic machines to the low priced flux/air spraying machines? We are going to be spraying an OA flux with 11% solids content. Are there a
Electronics Forum | Wed Jul 15 15:35:21 EDT 1998 | Michael Fogel
Hello Mark, Here in ECI, because the nature of our products, are using the method of press fit connectors in big numbers and although we have SMT components (around 200 per board) as well as T/H components we still preferred to use press fit because