Out of curiosity, what is your top side peak temp @ reflow? Have you inspected the boards prior to SMT (at your 5DX machine?) Also, have you tried to run the board through reflow with out any parts or bga placed and inspected? I how long are you in
Electronics Forum | Mon Jul 28 16:48:54 EDT 2008 | pcbbuilders
my oven has a built in profiler, it works fairly well, but it can not predict changes. my main concern was about the time right before reflow. i know that's where the flux is activated and i was worried that i may be spending too much time at the tem
Electronics Forum | Wed Dec 25 02:42:15 EST 2019 | sssamw
Yes, the barycenter causes drop off since only leads at one side, so a variation of re-flow oven, such as vibration or hot air flow, low re-flow time could help a little. So, how you solve this issue after many months?
Electronics Forum | Wed Sep 02 19:08:45 EDT 2009 | jlawson
Also consider electroltyics as some brands can only cope with one pass through reflow, 2 max. In Vapor phase 1 pass max is typical. Although depends on makers specs and what they say the device can withstand. main issue is Dielectrics get damaged , c
Electronics Forum | Fri Sep 16 14:12:23 EDT 2011 | jtownsend
Anyone have experience or advice to help prevent SMT reed switches from being blow out of position during re-flow? We are using a Heller 1707 MK 3. Is it possible to adjust air flow in the oven or do we need to glue before placement??
Electronics Forum | Tue May 20 06:00:33 EDT 2008 | roc2x
Im qualifying a new PCB. I run 2 diff supplier. Supplier A has Zero failure. Supplier B has 4 failure all having Lifted PAD on Bga same location and same location pads that lifted. How can I prove that the PCB have problem? Input : Both run in same o
Electronics Forum | Thu Sep 03 11:38:28 EDT 2009 | dyoungquist
I'd be more concerned with the pcb itself then I > would be with standard SMT components. Are you > using a PCB with a high Tg? (170 degrees C or > greater) The circuit board material is NP-170B (Nan Ya Plastics Corporation). It has a Tg of 170
Electronics Forum | Fri Sep 16 19:46:55 EDT 2011 | jlawson
I have seen this on Heller1707 machines also for LED devices. The same job was run on anthoer brand oven (Rehm) and no issue. I think Heller Blower velocity can be a little on higher side as is a low inertia heating system and they have to make up f
Electronics Forum | Fri Dec 07 06:05:58 EST 2018 | cyber_wolf
63/37 goes from solid to liquid. It melts and solidifies at a single temperature. You can add a percentage of silver and get a slight "pasty range" for a couple seconds. I have never seen a temperature change in a profile keep this from happening w
Electronics Forum | Mon May 13 06:38:41 EDT 2019 | relaycz
You need to give us a little more information. 1. What is the size of your panel? 2. Are there any heavy components? 3. What is the thickness of your board panel? 4. What kind of oven are you using? 5. Is it only a recent problem or ongoing one?