Electronics Forum | Wed Mar 24 21:51:23 EST 2004 | davef
Dreamy It sounds like you are having fun in your new job. Saponifier. Alkaline chemicals, added to water, that convert rosin/resin flux residues in the water to soluble soaps. Generally, saponifiers are better if used in an aggressive spray-in-ai
Electronics Forum | Tue Apr 13 22:48:11 EDT 2004 | Ken
I assumed the balls were tin/silver 221C or tin/silver/copper 218C liquiduous....but, this is obviously not the case. It looks like you balls are almost pure tin (mp=238C) You are correct. This is exactly the same as using 10/90 high temp balls o
Electronics Forum | Thu Jun 10 16:23:11 EDT 2004 | davem
Hi Grant, In previous positions I've had experience with the Fuji CP43, CP6, CP642, CP643, CP65, IP3 & QP242. In operating, training and process engineering capacities. Presently, I'm working with 2 SMT lines (in a process engineering capacity) wit
Electronics Forum | Mon Jan 09 18:51:05 EST 2006 | grantp
Hi, I have used both MYDATA TP9, MY9 and more recently MY12. MYDATA machines are just not accurate, and we did everything possible, and every kind of upgrade they had. We ended up putting in Fuji XP based machines, and the differences are very notic
Electronics Forum | Wed Jun 23 12:25:13 EDT 2004 | Cal
JD- I have used a few of GlenBrook's machines.. Jewel Box 70, Jewel Box 90, and RTX-113. Currently we have the RTX -113 on our shop floor as we speak. I like the machine but wished I would have went for for the angle viewing option or even the BGA so
Electronics Forum | Wed Aug 04 00:17:41 EDT 2004 | Shean Dalton
Additionally, increases in temperature can increase the water's rate of reaction with the flux. Sometimes, only a 5 degree change can make the cleaning difference. If the flux inconsistently presents itself, then the likely cause is something in
Electronics Forum | Tue Aug 10 15:28:54 EDT 2004 | Shean Dalton
Because the HASL process most deal with bare metals, HASL flux residues are generally more active than solder paste residues. Typically a Rosin Active (RA) flux is used in the HASL process. These flux residues should be removed from the bare board
Electronics Forum | Mon Aug 16 11:58:29 EDT 2004 | Dreamsniper
I've worked with a Vapor Phase Oven a semi-automatic and a manual oven for evaluation. They worked fine and produce better grain of solder joints. The fluid that you need depends on the solder temperature that you require. I've used a 200'C fluid for
Electronics Forum | Thu Sep 02 10:24:35 EDT 2004 | dj_jago
Greetings from the UK: I have been quite fortunate to lead (no pun intended) our company towards lead free sooner rater than later. One of our customers produces a product which is refurbushed every 6 months or so and sent back into the market. A
Electronics Forum | Tue Sep 14 19:47:16 EDT 2004 | davef
use something other than HASL. "The rest of the world seems to be processing with no problems..." [Hello!!! Earth to Carol. This is a test.] Things you are considering could be more trouble than they�re worth. "1) Reduce via hole size" [If you re
DONGGUAN KINGSUN AUTOMATION TECHNOLOGY CO.,LTD is a company which mainly provide used and new SMT parts, provide repair SMT key parts service,new/used SMT machine trading,SMT consumables and Peripherals equipment,Clean room, ESD..
Manufacturer's Representative / Manufacturer / Equipment Dealer / Broker / Auctions / Distributor / Consultant / Service Provider
3th, Tangchang 3rd Road, Hengli, Dongguan City
Dongguan, China
Phone: 008615629932323