Electronics Forum | Mon Nov 27 08:05:50 EST 2006 | davef
There is no standard for a strain gage measurement of allowable deflection of a board or a fixture. It's possible that your fixture is causing the BGA cracking that you see. What protion of the BGA is cracking? If it is the solder connection, sear
Electronics Forum | Wed Nov 29 01:12:12 EST 2006 | callckq
Dear Davef, Thanks for your input...The crack happen at the pad/solder ball interface..Pls review the new thread that I post just now with title called "BGA BALL CRACK AT PAD/SOLDER BALL INTERFACE" Thanks!
Electronics Forum | Sat Nov 25 21:26:55 EST 2006 | callckq
Dear all, I have an issue here where we found BGA crack. Understand from friend, we need to study any possiblity of our own jig or fixture cause this problem via strain gauge measurement..My question: Is there any standard @ specification establish
Electronics Forum | Sun Apr 16 14:37:25 EDT 2000 | Roberto Navarro
Hi, I work for Nortel and here rework BGA'S we use DRS22 rework station and CRT 2000 X-ray inspection. The main problem is put again the BGA on the PCB because you need reboling the PCB and you could damage the soldermask. Talking about Air-vac is ve
Electronics Forum | Fri Jun 19 09:45:21 EDT 1998 | Mike Cox
Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. Mike
Electronics Forum | Sat Mar 15 01:03:10 EDT 2008 | callckq
All, What if BGA solder crack do exist after the shock test? Its happen at the corner of the BGA. Base on your experience, what are the potential root causes? Thanks, Sean
Electronics Forum | Thu Sep 07 03:57:39 EDT 2000 | Steven Cheung
Does anyone know of a freely-available document which discusses the main considerations of BGA assembly and inspection (x-ray?). l need to know about pad sizes and inspection standards and when to underfill and when not to etc.. l am looking at ass
Electronics Forum | Tue Jul 09 15:20:19 EDT 2002 | pjc
When you look at the capabilities of Combo machines they tend to sacrifice performance when compared to separate X-ray and AOI machines, meaning they don't do either the X-ray or AOI operations as well as a machine that was designed to do only one. A
Electronics Forum | Wed Mar 12 07:33:40 EDT 2008 | callckq
Hi All, One PCBA failed test after went through the Shock Test(Vibration) and suspected to be BGA solder ball crack. We performed dye and pry and found PCB's pad lifted with red mark ink penetrate pad underneath, what does this mean? Can I say the
Electronics Forum | Mon Jul 08 13:49:10 EDT 2002 | msjohnston
HI, We are looking into expanding our current x-ray inspection from manually inspection one panel per lot to 100% automated inspection for all of our BGA and CSP builds. We have 100% manual inspection at the end of our SMT lines and we are consideri