Electronics Forum | Fri Jan 08 10:11:15 EST 1999 | Tim
This is a question for those of you who actually assemble components onto a board. Any idea what the "industry standard" is for fall out on assembled PCB's? I realize that the controls put in place in your processes will effect your overall quality
Electronics Forum | Sun Jan 10 08:44:32 EST 1999 | Dave F
| | | HI! I am a package engineer in Korea. I have some reasons | | | to desolder excessive solder at the lead of TSOP and TSOJ | | | after removing them from the board. The way with solder wick is too time-consuming and depends on the operator. |
Electronics Forum | Wed Dec 23 03:33:14 EST 1998 | Charles Stringer
Can anyone recommend a solder stop that can be applied by our PCB supplier. Our current material form Tamura Kaken is causing problems. The material should be capable of withstanding 1 Surface mount IR reflow cycle and 1 wave solder cycle. We need t
Electronics Forum | Fri Oct 23 04:16:16 EDT 1998 | Tony B
| | My company is looking for higher density for card layout. One suggestion has been locating active components packaged in SOT's and SOIC's on the B-side of the card. This in turn will require wave soldering of the above mentioned components. When
Electronics Forum | Tue Oct 13 18:28:51 EDT 1998 | Graham Naisbitt
Upinder, Using IPA does not cause the residue, it simply exposes it. Given that all fluxes leave reisdues, it follows that these MUST be benign - but how do you know, and how do you control it. You are using flux to remove oxides and give you a go
Electronics Forum | Thu Oct 15 13:55:43 EDT 1998 | Steve A
Dave, The first step would be to learn to accept the residue. IPC class 2 has no problem with it. If that is not possible, I am not sure why a no clean is necessary- but I will take your work for it. Alcohols will dry out the residue, and turn it
Electronics Forum | Thu Oct 15 16:39:07 EDT 1998 | Dave F
Steve: I thought Kyzen products were "additives" to either aqueous or semiaqueous inline or batch machine cleaning processes. I'm trying to clean the no-clean residue from a few components that can not bear to see water. Can you use Kyzen products
Electronics Forum | Tue Oct 13 12:58:18 EDT 1998 | Justin Medernach
| We suffered our first blood letting because of razor sharp edge clamps (DEK 265LT) and operator giving it the finger. While positioning magnetic tooling pins, one of our best slipped and really sliced off a part of his main digit. This will impact
Electronics Forum | Tue Oct 13 16:26:26 EDT 1998 | Earl Moon
| | We suffered our first blood letting because of razor sharp edge clamps (DEK 265LT) and operator giving it the finger. While positioning magnetic tooling pins, one of our best slipped and really sliced off a part of his main digit. This will impac
Electronics Forum | Wed Oct 07 14:55:17 EDT 1998 | Joe P.
| | I am trying to find out, what possibilities I have, to print solder paste on a board, when the task is to have 120 Microns thickness for the biggest part of the board (85% of the real estate), and then have 250 Microns of thickness on the remain