Electronics Forum | Sat Aug 28 14:16:18 EDT 1999 | JohnW
Doug, Have you tried running the boards at an angle to the wave of between 15 - 30 degree's ? I've done this on a few boards to eliminate short's and I believe it will work on your problem very sucessfully. Best thing to do is get your wave solder c
Electronics Forum | Fri Jun 18 13:48:37 EDT 1999 | Earl Moon
| We currently use HASL on all of our boards and I would like to move to something else. I have sampled some boards with Entek OSP and I loved it, the problem is we have plated mounting holes on just about every board we make. Does anyone have info
Electronics Forum | Fri Jun 18 14:06:15 EDT 1999 | John Thorup
| | Now don't everyone jump on this at once, but it seems time for me to send out copies of my not even close to being dated copy of an article about HASL. Though it was published in 1992, in Printed Circuit Fabrication Magazine, and it got rave revi
Electronics Forum | Mon Jun 14 14:30:42 EDT 1999 | Deon Nungaray
| | | | | Hello all! | | | | | Recently we got a problem about the Funtional test. Some boards passed tests by using the auto-fixture(vacuum), but failed by using manual test fixture(need to plug CPU, DIMM etc.). The error symptom is no picture. We d
Electronics Forum | Wed Apr 28 11:47:34 EDT 1999 | Frank Boyko
| | We use Immersion Gold (AuNi) for our 20 mil pitch and BGA boards. | | Lately, we have been having solderability problems with boards with this surface from some of our suppliers. | | | | We are considering trying boards with White Tin solderable
Electronics Forum | Tue Dec 08 16:53:41 EST 1998 | Ryan Jennens
Hey there Dave! We used to use a batch cleaner when we used water-clean paste. It was similar to a dishwasher, except that it had a digital menu for entering the number of wash cycles, water temp., amount of saponifier (we just used DI water),
Electronics Forum | Mon Nov 02 22:57:02 EST 1998 | Kelly Gossman
Micheal, What does your profile look like for the wave? What profile does your flux say you need? My guess is it is not your profile, our testing with solder balls found that the mask on the boards was the largest contributor to solder balls. Wha
Electronics Forum | Thu Oct 08 22:20:44 EDT 1998 | Dave F
| | | I am trying to find out, what possibilities I have, to print solder paste on a board, when the task is to have 120 Microns thickness for the biggest part of the board (85% of the real estate), and then have 250 Microns of thickness on the rema
Electronics Forum | Fri Oct 09 04:08:45 EDT 1998 | Thomas Blesinger
| | | | I am trying to find out, what possibilities I have, to print solder paste on a board, when the task is to have 120 Microns thickness for the biggest part of the board (85% of the real estate), and then have 250 Microns of thickness on the re
Electronics Forum | Fri Oct 02 16:49:33 EDT 1998 | Dave F
Benji: I tend to agree with you that assemblers shouldn't wear make-up. I'm unsure what first level assemblers are tho. I've been down that finger cot/glove route ... 1 If someone is going to smear facial or cosmetic oil on a board, they can do