Electronics Forum | Fri May 01 14:00:59 EDT 1998 | Chrys
I've never seen this before. Today, I got this tombstoning on Tantalum Capacitors (Okay, I saw that before) Here's the part that seems weird to me: -They didn't tombstone onto a termination - they went onto their sides! That's right, both terminati
Electronics Forum | Sat May 02 00:51:14 EDT 1998 | Rick
I agree with Steve...most certainly a placement occurance. I've seen this on many occasions with Panasonic equip. Change your feeder first and then check your component packaging. | I've never seen this before. Today, I got this tombstoning on Tan
Electronics Forum | Fri Apr 24 23:03:28 EDT 1998 | Mikec
| I inherited a DI system that's um...not in good shape. | I would be forever indebted to anyone who could help me | with several problems related to this. | Flow rate 3.5-5GPM | Incoming pressure:50PSI | Application: deionized water provided to Elec
Electronics Forum | Thu Mar 26 23:17:04 EST 1998 | Marty Fox
| | | Is there anyone out there required by their customer to clean the finget tab contacts even after using noclean paste? We have been asked to clean even though we don't have any flux residue on the contacts. Any ideas? | | | Mike | | | | Yes a
Electronics Forum | Mon Mar 02 09:45:08 EST 1998 | Justin Medernach
| Can anyone advise a good starting point for a temp profile for | on 0.05" and 1206 component boards? These boards are simple | by todays standards and do not contain any fine pitch or | other special components. | Thanks in advance... | MM Mike,
Electronics Forum | Mon Mar 30 16:39:04 EST 1998 | Tony Arteaga
Hello there, I am currently doing BGA repair and basically I am applying the same process as Mike sujested. It is actually the way to go when creating a profile. The next process is re-balling your package, that is if you whant to use the same compon
Electronics Forum | Wed Jan 28 19:39:08 EST 1998 | Steve Gregory
| | What is the lifetime for a typical solder paste ? | | How long can boards be stacked waiting before the paste goes off ? | Lifetime and tack time depends on: | - Manufacturer | - Flux/mixture | - Environmental conditions | Typical lifetime is dep
Electronics Forum | Mon Jan 19 20:25:52 EST 1998 | Steve Gregory
| I have a problem! The solder on my pc boards look great comeing out | of my reflow oven. They go thrue the rest of the prossese | and at the end at the qc station it's cold or whitish or gray not shiny. | does any one have a idea on how to correct
Electronics Forum | Mon Aug 27 15:50:05 EDT 2001 | seand
Hello Everyone, The MPM UP 3000 may be a good bet for your Screenprinting application and I am aware that there are a few in inventory at Speedline Technologies (MPM) that you should be able to get with a warranty for a good price. I know wide vers
Electronics Forum | Wed Sep 05 08:50:04 EDT 2001 | davef
No arument with others comments about moisture, but taking a different tact, consider that the volitle elements of the solder paste disppear as a function of the amount of time the paste is out of the container. [Maybe as a function of solder paste