Electronics Forum | Mon Aug 04 09:30:16 EDT 2008 | grics
If you have concerns, you can look at the datasheet for each component or contact one of their application or materials engineers and find out what the components are rated for...process-wise. IE, how long can I be in the oven with this part, at what
Electronics Forum | Fri May 15 21:39:48 EDT 2015 | jlawson
Reflow.. 1.Rehm (Germany) - Best in Class Best overall process stability heating system ( Alot of makers have started to copy there VX heating arrangement ). COnveyor chains can be a bit more attention in terms of maintenance on rehm , but if foll
Electronics Forum | Tue Jul 09 15:20:19 EDT 2002 | pjc
When you look at the capabilities of Combo machines they tend to sacrifice performance when compared to separate X-ray and AOI machines, meaning they don't do either the X-ray or AOI operations as well as a machine that was designed to do only one. A
Electronics Forum | Thu May 24 09:11:12 EDT 2001 | Grant Petty
Hi, I would agree. We purchased a TP9 just the slow machine, but we were a small company at the time, and it worked fantastic. Almost no maintenance, and it's a dream to changeover. The serivce in Australia is also very good, but that does not appl
Electronics Forum | Fri May 15 14:50:40 EDT 2015 | emeto
My top 3 printers: 1.DEK 2.MPM 3.EKRA Top 3 ovens: 1. BTU 2. Vitronics 3. Heller or Electrovert
Electronics Forum | Thu Jun 27 11:22:03 EDT 2002 | robbied
Hi there. We have had an out of control reflow oven that has allowed its temperature to fluctuate by up to +/- 20 deg C from set point in very short periods of time. We found the root cause of the problem and fixed it, but by then we had already run
Electronics Forum | Thu Nov 15 09:29:29 EST 2012 | anvil1021
Maybe this piece of information will help. In China (just returned from visit) there are many factories that are using a dual temperature process using SAC305 or Sn100C and 42/58. Apparently this allows them to run their through hole parts through re
Electronics Forum | Fri May 22 17:48:48 EDT 2015 | aemery
It's your first line, go with established manufacturers. Whether new or used it ultimately comes down to does the tool do the job and how well is it supported (labor/parts) if it does break down. I am a former field eng. with Speedline and now run
Electronics Forum | Fri May 22 12:42:43 EDT 2015 | deanm
Sr. Tech, you are right in that there is no verification of the profile. We are a Class 3 high mix OEM. We have visual inspection after SMT. We have not seen problems with wetting, grainy solder, cold solder, charred boards, etc. that would indicate
Electronics Forum | Mon Apr 12 19:28:26 EDT 1999 | Tom B
Netters, When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? 1. Kester 293 no clean 2. 2.1 C/s for 30s to 150 C 3. .5 - .7 C/s for 60s to 185 C 4. 1.5 C/s u