Electronics Forum | Mon Nov 23 23:13:53 EST 2009 | wyko007
I recently purchased a CSM84VZ Type PA130460. The machine did not come with any reference material and its a pain learning by creating errors. Can anyone share with me any related material that is necessary to get the tool running smooth. Thanks in a
Electronics Forum | Fri May 11 02:54:48 EDT 2007 | pima
Im using this for example to introduce new product and new part numbers and shape. Ive got in notepad list with all components and macro is importing one by one every and putting inside FujiFlexa. Its work like in visual basic. so u can generate macr
Electronics Forum | Wed May 16 08:50:52 EDT 2007 | pima
Hello For long time we are fighting with problem to reduce/eliminate electrostatic charge caused by board cleaning machine- we re using Teknek machine. Maybe u guys have idea or from ur experience u know how to reduce electrostatic charge at sensit
Electronics Forum | Tue May 22 03:11:40 EDT 2007 | Frank
We also keep our pot just below the liquidous state over night. It takes a lot less time to get it to temp than a cold pot and we aren't creating dross over night. If you have been shutting down over night for some time, then you can get an average
Electronics Forum | Mon Jun 11 18:52:19 EDT 2007 | darby
Verbal history says it was the wave. Written history says it was a glue gun plugged into 24hr power and left on. Destroyed the top floor of the then 3 year old factory. "PLANT'S on fire" -good one!! I thought I paid good money to keep that vid out of
Electronics Forum | Fri May 18 10:56:09 EDT 2007 | patrickbruneel
Hi smtnetters, I�m looking for reference material preferably graph�s displaying the viscosity and surface tension vs. temperature for standard Sn63 Pb37 alloy. Plenty of reference material is available on pure metals but can�t find anything on the
Electronics Forum | Tue May 22 12:27:04 EDT 2007 | cyber_wolf
I would consider calling Kester and telling them they need to send their people out. I could not really see mesh size being an issue on anything 20mil and above. There are several other issues that can cause aperture clogging as well...: Incorrect
Electronics Forum | Thu May 24 02:09:29 EDT 2007 | einat
I would like to learn more about the differences between the two. Which one do you recommend more and why? Also if someone can stand on the differences between: MPM UP 3000 HI E MPM UP 3000 MPM UP 2000 HI E MPM UP 2000 Any information would help!
Electronics Forum | Mon May 28 03:36:46 EDT 2007 | aj
Hi All, We have a QFP device that is struggling to achieve acceptable solder joints. I have noticed one or two of the components shifting during reflow. I can adjust the Blowers but I dont have any issues on other boards. This seems to be a straigh
Electronics Forum | Fri Jun 01 22:09:03 EDT 2007 | mika
Hi Aj, What type of QFP are we talking about? We had in the past big problem with QFP-304 0.5mm pitch from ALTERA. Similar as you describe. Note. No problem with QFP-256 or QFP-196 0.5mm pitch, or anytying less than -304:s Can You be a little bit mo