Electronics Forum | Mon Aug 09 11:34:25 EDT 2004 | Woodsmt
I am looking for data / info on how flux may contaminate the solder in a Wave. I have a customer who requires a no clean process. Our wave is equipped with 2 separate fluxing systems and I would like to use OA in one and the No Clean in the other. Th
Electronics Forum | Mon Aug 09 13:43:25 EDT 2004 | gbeck@optimumdesign.com
We just spent $100 and updated our Vitronics 800 oven software and it only shows only ONE zone for the entire machine. Vitronics wants $2,000 for a service call! Does anyone know what config file or software menu changes the number of software zones
Electronics Forum | Tue Aug 10 09:26:49 EDT 2004 | davef
You should be able to solder to brass - check with you flux supplier to get their recommendations. The flux you are using may not have enough activation to breakdown the oxides on the brass surface. A word of caution - brass (copper and zinc alloy)
Electronics Forum | Tue Aug 10 06:45:54 EDT 2004 | Snehal Acharya
Hi to all, I'm facing a soldering problem with one of my series of Product, since we were using a two different kind of PCB 1.GE(Glass Epoxy)2.PP(paper phenoline) in later PCB if i will use the same profile of the GE then it will get backed more & i
Electronics Forum | Wed Aug 11 00:57:15 EDT 2004 | vinitverma
Hello, I may be able to help you on CSM84 series. Please write in details the problem that you are facing. Are you able to start the machine? If not, what is the serial no. and year of manufacturing of the machine? What is the message that you get w
Electronics Forum | Mon Aug 16 13:18:46 EDT 2004 | davef
You bet our reponse changes. Q2R: Hard gold thickness is 4 to 10 u" for Au and 300 to 400 u" for nickel A2R: This is a hard gold spec?? It looks like a ENIG spec. Although, the Ni is quite heavy, 150 uin is sufficient for most applications. The gol
Electronics Forum | Fri Aug 13 12:49:15 EDT 2004 | WALSTIB
Russ is correct, The efficiency number, or machine operating ratio, is more relevant in a HVLM environment than a HMLV senario. I have found that in HVLM, a desirable number would be cetianly 80% plus. Low 90 is not unrealistic. One must consider
Electronics Forum | Thu Aug 12 14:08:59 EDT 2004 | pgarsoe
This forum is for free use for all. Some times you see a question that is raised that your company's product would be a solution. Fine, post a general statement to that effect and a reference to where they can get more information. BUT DO NOT USE TH
Electronics Forum | Tue Aug 17 10:44:44 EDT 2004 | cyber_wolf
Carl, That machine looks way expensive. We found a used Fuji microscopic jig for 3500.00 It came with the master jigs and master tapes. It doesn't have all the bells and whistles, but it does exactly what it is supposed to. John, I am curious as t
Electronics Forum | Fri Aug 13 18:38:47 EDT 2004 | russ
Your paste manufacturer will have the best guidelines for you. Different paste types and manufacturers sometimes/usually require a little bit different setup. I would also contact your printer manufacturer. As far as stencil concerns the larger/be