Electronics Forum | Thu Oct 12 12:22:52 EDT 2000 | stefano bolleri
This is a question about LCDs (Liquid Crystal Displays) packaged as SIPs or DIPs. My question is: can they be wave-soldered? I found process recommendations on Web pages of several LCD suppliers, and they pretty much all say that LCDs should NEVER be
Electronics Forum | Tue Oct 17 12:15:19 EDT 2000 | NLykus
Dave, Current process is Insert through hole components topside Dispense SMT glue Place SMT components bottom side Glue cure Insert 1 through hole component by hand Wave Wave temperature is 480oF Topside preheats in D.O.E ranged from 99oc to 108oC
Electronics Forum | Wed Oct 18 16:41:35 EDT 2000 | Dave F
It's unrealistic to think that two materials with the following disperant properties would have the same reflow profile. From http://www.norplex.com/Carrier.htm Physical Properties / NEMA FR-4 / NEMA CEM-1 Glass transition temperature �C / 130 / 10
Electronics Forum | Wed Oct 11 16:24:35 EDT 2000 | John Thorup
Hello Antonio ASPECT RATIO = the ratio of one dimension to another as in the ratio of the thickness of a stencil to the width of the aperture. For instance, a 10 mil aperture in a 5 mil stencil will have an aspect ratio of 2. This is aperture width
Electronics Forum | Wed Oct 11 10:29:28 EDT 2000 | G. English
Try the following steps : FIRST CHECK THE ARCHIVE for further information, it WILL help you. Step One : What�s the chemical analysis of this white res? Obtain a sample. It could be tin, rosin, or something else??? Step Two : The fastest way I know
Electronics Forum | Fri Oct 13 05:21:08 EDT 2000 | Robert Steltman
Looking at the original post, it seems that the white residue is formed on the board after wave soldering and becomes evident when it has been left standing for a while. From what I understand, it seems that the solids content of the "no clean" flux
Electronics Forum | Mon Oct 09 21:17:24 EDT 2000 | Dave F
I don't get the no-lead thing, but it's good marketing so, whose to fight it? Yano? If I didn't get the no-lead thing, I'm double clueless about bromine. That is until I read a recent (8/00) article in PCFAB magazine. I away thought of bromine as
Electronics Forum | Mon Oct 09 10:37:25 EDT 2000 | DL
John, I hope your figures or numbers are part of your SPC process. Our management loves this stuff. I think the production line, world class or not would reflect the attitude of the people working on it(keep that between you and me) management does
Electronics Forum | Sun Oct 08 14:09:45 EDT 2000 | dtm
Ok here's the story...My company has recently started an in house smt line. (we have been mfg thru-hole for years). We hired a smt op and the most of the rest was from reading and previous experiance from other employees/engineers. Our test departmen
Electronics Forum | Sat Oct 07 04:02:50 EDT 2000 | C.J. Long
Good morning, All: I am from PCB shop and one of our customer is experiencing solder bridge on 16 mil pitch QFP( immersion gold finish). Land width requirement is 8 +/- 1 mil measured over top of of land and our mean is 7 mil. Bottom land width is 8