Electronics Forum | Tue Jul 29 03:32:19 EDT 2014 | cmchoue
The solder in MB become to yellowish after thermal test (100 oC/12HR) I think the problem that is flux residue and I really want to know the principle that why it color change Thanks!!
Electronics Forum | Fri Aug 01 06:54:22 EDT 2014 | tegel
Hi, I don't have any solution to the problem, but the component is an EMI-filter and not part of the machine. // Tegel
Electronics Forum | Fri Aug 01 09:21:28 EDT 2014 | jimmyboz
Does it error during nozzle center check, if so, manually switch all holders to small, try center again. It should do about 8 small nozzle centers before error, if so this helps rule out the 10th station, if not check the 10th.
Electronics Forum | Fri Aug 01 11:57:56 EDT 2014 | kurtiss
It turns out it was a misaligned fiber sensor on station 12?, the after rotation nozzle verification.
Electronics Forum | Thu Aug 07 12:58:59 EDT 2014 | kahrpr
One of the things you need to know are the parts you are building Flight Critical. Meaning if the board fails will it bring down the aircraft. Or non critical meaning one of the over head light will fail as an example this determines how much latitud
Electronics Forum | Sun Nov 16 19:05:45 EST 2014 | warwolf
Seen it. We use a lead free process, sometimes our supplier will use a lead process silk screen that burns at a lower temp. The HASL coat was still SN100CL.
Electronics Forum | Mon Oct 13 18:15:38 EDT 2014 | ilavu
Hey rob, make sure you do the changer setup. That procedure looks at the fiducials on the changer and adjust the position for nozzle change. It is in system setting. Motor or amp is not easily go bad. I have machine from 92 and never had problem with
Electronics Forum | Tue Nov 11 13:25:17 EST 2014 | jimmyboz
I do not recall that "TEACH" ever worked. Even if it did, there is no way to save this data to the MCS. After you see that a fiducial cannot be found, change Xa-Ya in the program at the MCS to find it, and of course, re-transmit. Good Luck
Electronics Forum | Wed Feb 25 11:47:09 EST 2015 | emeto
What are the chances for redesign the board or use substitute for the current tall part? Sometimes the hassle you want to go through could be avoided. How about change the box the device goes to or modify/ customize it to fit this part better in?
Electronics Forum | Thu Feb 26 21:35:21 EST 2015 | flyingsnow
Hi, has anyone experienced discoloration of cured non-conductive epoxy? It turned from white to deep red. The parts were returned from customer and we noticed the color change and wondered what could cause epoxy discoloration.Thank you!