Electronics Forum | Fri Nov 11 04:13:23 EST 2005 | arnold
we are manufacturer of molded type transformer and we soldered are units using wave soldering machine and then we washed the units to remove flux residue. what materials or any process for us to eliminate the process of washing after wave soldering.
Electronics Forum | Fri Jan 23 09:21:22 EST 2009 | sm2009
Hello, thanks to everyone that reply to my previous question. I have another request: is it possible to solder polyester capacitors (case 2220) with wave soldering process? Thanks! Regards, Stefano
Electronics Forum | Thu Jan 29 12:57:37 EST 2009 | wavemasterlarry
Only if it has exposed ends on the end.
Electronics Forum | Fri Nov 11 06:58:03 EST 2005 | bk
A little more information on your current wavesoldering process would be helpful in helping you. Information like what kind of flux your are using,how you are applying the flux,what preheat temps you are using,and your conveyor speed. Without knowing
Electronics Forum | Mon Jan 31 12:24:24 EST 2000 | Dave F
Robert: Several points: 1 Dross is a mixture of various things with no "fixed" composition: � The obvious things are metal oxides mixed with metal and this can vary in color with temperature and composition - remember some intermetallic oxides form
Electronics Forum | Sun Sep 09 16:03:50 EDT 2007 | davef
Wave Optimizer-person Help us understand how your "excellent wave solder guide called 'Take No Prisoners' that includes instructions for attacking and eliminating solder balls and preventing their recurrence" will help Joris resolve his / her issues
Electronics Forum | Thu Feb 26 16:49:57 EST 1998 | specnor tecnic corp
we have some rebuilt wave soldering systems in stock ready to be shipped. epk-ii smt with lambda wave, chip wave ,omega wave. 4 preheaters,jacking stand roll out computer control. machine is in a great shape. another machin upk15f with 6 preheaters
Electronics Forum | Tue Sep 12 04:48:26 EDT 2000 | Daniel
Is there a risk of popcorning plastic components during wave soldering? (The PCB is first surface mounted, reflowed and washed. It is sometimes left in air environment for as long as 48 h before the throgh hole components are mounted and they are wa
Electronics Forum | Fri Dec 01 03:23:50 EST 2006 | Joris Groot Koerkamp
For better quality in our wave solder process i want to start with an improvement project (to eliminate solderbridges). Does somebody know what are reachable ppm rates for solderbridges in a wave soldering process? The boards are simple. Only some
Electronics Forum | Wed Jan 07 05:53:05 EST 2009 | sm2009
Hello, does anyone know if it's possible to wave solder 0402 components? Are there drawbacks? Where can I find technical details about recommended footprint and glue point? Last question: are there suggestions about wave soldering for ic with 0,635mm