| Looking for anyone who has experience with high temperature soldering. Need to determine why solder joints are failing. Thermocycling of unit is -40C to +140C, 30 minute dwell time, 10 sec. transition time | Your help is appreciated | Ed Holton |
Electronics Forum | Tue Apr 21 06:23:37 EDT 1998 | Michael Nedley
I teach Industrial Electronics courses at a 2 year College. We use Analog/Digital trainers with standard Breadboards for full size IC's. My problem is this, Alot of people in the manufacturing Industry have been gracious enough to send samples o
Electronics Forum | Thu Mar 26 11:25:21 EST 1998 | Earl Moon
In December and January (1997 & 1998) a number of people requested information regarding component cracking. I overlooked this until recently thinking design and process requirements were violated. After reviewing the last 14 months consulting effort
Electronics Forum | Mon Mar 30 16:02:44 EST 1998 | Michael Allen
| We have successfully put .016" vias in .030" pads. | There is no issue with .030" solder balls, since | the actual volume of the .002" via in pad is small | compared to the ball+solder paste volume. | We did notice random bubbles where, apparentl
Electronics Forum | Mon Mar 16 04:46:25 EST 1998 | Grant Petty
We have just go another batch of PCB's from our loaders, and some of the boards are severely warped. The boards are PCI cards and one of the boards is 9mm out at one end. The PCB is 210mm long and 4 layers. I am wondering if anyone knows what could
Electronics Forum | Mon Mar 16 16:57:59 EST 1998 | Earl Moon
| We have just go another batch of PCB's from our loaders, and some of the boards are severely warped. | The boards are PCI cards and one of the boards is 9mm out at one end. The PCB is 210mm long and 4 layers. | I am wondering if anyone knows what
Electronics Forum | Mon Mar 16 09:07:14 EST 1998 | Justin Medernach
| We have just go another batch of PCB's from our loaders, and some of the boards are severely warped. | The boards are PCI cards and one of the boards is 9mm out at one end. The PCB is 210mm long and 4 layers. | I am wondering if anyone knows what
Electronics Forum | Sun Jan 11 11:28:14 EST 1998 | Bob Willis
Most componnent cracking is mechanicaly produced a guide to causes of capacitor damage is included as a download file on my web page www.bobwillis.co.uk I feel that the supplier is looking to blame some one else. IPC make comment on pre heating chip
Electronics Forum | Sun Jan 11 11:28:12 EST 1998 | Bob Willis
Most componnent cracking is mechanicaly produced a guide to causes of capacitor damage is included as a download file on my web page www.bobwillis.co.uk I feel that the supplier is looking to blame some one else. IPC make comment on pre heating chip
Electronics Forum | Mon Dec 29 14:42:00 EST 1997 | justin medernach
| Hello all, | I have experienced broken ceramic SMT parts. Most of the time, | we have found fractured inductive beads. Once in awhile, we find | broken Ceramic Caps. All parts we use are 1206 form factors and | we use tape and reel... | Michael