Electronics Forum | Fri Jul 20 17:09:10 EDT 2001 | davef
Circuits Assembly magazine 09/99 "Defluxing with Ultrasonics" by Les Hymes. [There's more but I can't find it right now. I'll add to this as I find the junk, er very nice stuff.] J-STD-001C states that its OK to use ultrasonics for cleaning so lon
Electronics Forum | Fri Jul 20 10:35:34 EDT 2001 | slthomas
David, I've thought about doing this also with no clean boards that were poorly cleaned following a misprint (and subsequently reprinted, populated, and reflowed) but have shyed away because of the potential for damage to components from the ultraso
Electronics Forum | Tue Jun 24 12:42:35 EDT 2008 | slthomas
Your flux residues may be acceptable for your drain, but the solder balls won't be. You'll need to filter and dispose of the filters per your local city, county, and state regs. Either that or just boil the water off and dispose of the dry remains wi
Electronics Forum | Tue Jun 24 13:46:21 EDT 2008 | bschreiber
I know it is not what you want to hear, but first and foremost, you must consult your local regulating agencies and here is why: Solder paste contains heavy metals. We are all familiar with the problems associated with lead, but lead free solder pas
Electronics Forum | Thu Oct 26 11:49:54 EDT 2006 | sms_don
CW, The good news is that you are not trying to use SAC paste with SnPb balls for that would be a void generator due to the ball being liquidous while the SAC paste is still in a flux cleaning stage. Two points to consider: One, voids are not an i
Electronics Forum | Fri Jul 06 03:23:01 EDT 2001 | kennyhktan
Hi there Steven ! Please allow me to share some of my problem we're facing here with you. Here are a few points that I suggest you should check on your current process:- (1)PCB - Component land partern design ? It is per IPC spec ? - Mask
Electronics Forum | Thu Sep 26 11:44:23 EDT 2002 | abelardo
Hello everyone out there in the SMT world. I have a dilema I'm currently running a board that has 3 csp's with a .75 mm. ball pitch and .3mm ball size. And 2 qfp's-160. The stencil is 4 mils thick and I'm using a 63/37 solder paste. My reflow prof
Electronics Forum | Thu Sep 26 20:43:51 EDT 2002 | davef
"OK. If the connection doesn't look like I expect it to look, how do I know that the metallurgy is correct?" Comments are: * There are no pictures that will get you though this. * You should expect that gold that is dissolved in Pb/Sn solder to make
Electronics Forum | Mon Sep 14 11:56:38 EDT 1998 | Ben Salisbury
| Our company currently donesn't have any type of sonic wash to wash boards that have been "miss printed" Wanting to know the best way to go about this. So what we are having to do is spray down the boards with alcohol and wipeing the solder paste
Electronics Forum | Wed Feb 23 22:38:28 EST 2005 | davef
We: * Cure 1B73 according to spec in a heat box, like a Blue-M * Clean nozzles [one set in use, one set being cleaned] in thinner in a bronson ultrasonic cleaner * Haven't evaluated coatings in years, but would do it according to J-STD-001C, Reqmnts