Electronics Forum | Tue Feb 11 22:28:25 EST 2003 | davef
What do you mean by "new information"? On final module testing: * If you have hypercorroded nickel and you detect it during final testing, you'll notice it. * If you have hypercorroded nickel and you don't detect it during final testing, you'll ship
Electronics Forum | Fri Mar 07 10:51:58 EST 2003 | MA/NY DDave
Hi O'Conner, I hope you also tell us what Universal-GeorgeW discusses with you. It is a little strange seeing his name on this list and his phone number. Gee I can give you his email address but won't.. Again distance engineering is tough. I woul
Electronics Forum | Fri Mar 07 15:20:11 EST 2003 | davef
O'Connor: IPC-A-610, section 12.4.4 SMT Soldering Anomolies - Nonwetting was added primarily to accomidate OSP boards. Heated flux is used to remove the 'lacguer'. So, you end-up with a copper colored border [or shadow] around the pads, where there
Electronics Forum | Fri Apr 04 09:28:59 EST 2003 | davef
Q1: Anyone has any ideas on how this post-SMT reflow solder joint could have changed to whitish joint? A1: Dunno. You need to tell us more. For instance: * What is the appearance of this white residue? [eg, glassy / coarse, milky colored / opaque,
Electronics Forum | Wed May 07 09:31:28 EDT 2003 | davef
We use uV Dymax glue for thermocouple attach sometimes, but don't like the remainder [anal] and loosing attach, sometimes. Roger Saunders, President Saunders Technology, Inc; said: PRO: � These products are easier to use than high temperature solde
Electronics Forum | Tue May 20 20:28:58 EDT 2003 | Mike Konrad
Dear Carl, My-my Carl, not sleeping well lately? No mater what you say, I believe this is a forum for SMT users, not SMT suppliers. When this or any other forum gets polluted with sales-spin, it is less valuable than if a �real� user provides his
Electronics Forum | Wed Apr 14 09:44:34 EDT 2004 | Vince Whipple
Frank, Your initial question about temperature profiling is a critical point to a good wave solder process. Especially if you have a No Clean flux. As recommended by many in the thread above, get the Process Data Sheet for your flux (this is not the
Electronics Forum | Fri Jul 04 21:09:04 EDT 2003 | ramanandkini
I have a CEM-1 PCB board with 35 microns copper. This is PCB is finished with SMOBC+HALS. We do solder SMT LEDs, but till date we do not have problems that you have listed. The LEDs are good & bright. It even passed high & low temp cycle tests (-40 t
Electronics Forum | Mon Jul 21 08:34:44 EDT 2003 | Don Bell
Blow holes/ pin holes in solder joints are the result of multiple root causes. Suggested analysis might look like this; 1) What method of solder preservation is used on the bare board. (hasl,enig, osp, etc.) HASL can leave unwanted flux residues,
Electronics Forum | Fri Jul 18 10:46:43 EDT 2003 | davef
If you are saying that you have discolored white tin at in-bound inspection, you have bad boards. The boards are fabricated incorrectly. Your fabricator is deficient. That is the GREAT thing about imm coatings. You can look at them and determine