Electronics Forum | Thu Sep 03 18:48:52 EDT 1998 | Pete Sorenson
| I am in need of possible causes and solutions to capacitors that are failing in the field. | Are there issues in our process that need to be | checked? | Some people said the problems are due to improper | storage. Others say it is thermal stre
Electronics Forum | Wed Sep 02 16:37:18 EDT 1998 | SMT-ASSY
We sent you our brochures through your Email address. SMT-ASSY Electronique Inc. offers training to operators, technicians, engineers or any other individuals that requires hands on training on hand soldering, board rework and the surface mount tech
Electronics Forum | Sat Aug 22 12:18:12 EDT 1998 | Tryin'
| Board shops and us, the user, have a lot on our hands. As far as getting traces - this is done using an etch resist before solder mask and the HASL processes are performed. So when in the process is HASL performed?? | With tin/lead plated boards,
Electronics Forum | Mon Jun 22 17:37:03 EDT 1998 | Dave F
| | | | hi all. | | | I am looking for a oven which can cure the conformal coating providing heat and the humid atmosphere. I am looking for a temperature range of 60 deg C to 80 deg C and a humidity range of around 80%. | | | Can anybody refer to
Electronics Forum | Thu Jun 18 20:57:12 EDT 1998 | Dave F
BACKGROUND: We just got back from a neighborly visit at one of our board fabrication shops. I saw something interesting. Their HASL machine was just short of being field stripped. The story I caught was, the air pressure from knives change over
Electronics Forum | Fri Jun 12 14:22:53 EDT 1998 | Ryan Jennens
| Hey all! | The wave solder warrior is back. I have found a flux which leave almost no residue (the least yet), but because of its super low solids content I absolutely cannot get topside fillets. The multi-layer, two sided board is on a pall
Electronics Forum | Tue May 26 14:50:07 EDT 1998 | Dave F
| | I'm reviewing my board fab spec. It calls for a minimum SnPb thickness of 50 microinches on HASL PWB's. I've looked at other specs that call out anything from 30 to 80 microinches, and others that just say the copper pad must be covered and sol
Electronics Forum | Thu Apr 16 14:09:04 EDT 1998 | Lou Madge
Dear Collegue, A seminar tittled "Things that you should know before selecting an alternative surface finish" will be offered on Friday, April 24 (during the week of the Nepcon East show) in Philadelphia. Topic that will be discussed include: Evalua
Electronics Forum | Thu Apr 16 14:07:49 EDT 1998 | Lou Madge
Dear Collegue, A seminar tittled "Things that you should know before selecting an alternative surface finish" will be offered on Friday, April 24 (during the week of the Nepcon East show) in Philadelphia. Topic that will be discussed include: Evalua
Electronics Forum | Wed Mar 11 10:58:58 EST 1998 | Earl Moon
| | What does the term "poor wetting" mean as a defect code ? "Poor" should mean unacceptable when surface (component or PCB solder termination areas) wetting does not provide acceptable solder joints. Unacceptable wetting of PCB solder termination