Electronics Forum | Fri Jun 18 11:33:16 EDT 1999 | Brian wycoff
| | first of all what is the technical term for the small amount of solder on a plated pad. we are getting poor screen printing gasketing on a 20 mil qfp due to this solder not being even or too high in spots and not covering the length of the pads.
Electronics Forum | Wed Jun 02 07:23:04 EDT 1999 | Earl Moon
To you all for comment and summary, The following things I like without endorsing (PCB/PCBA stuff - outside the great women in my life [many] and without [mostly]): 1) A good set of design rules 2) A good set of design rules meeting producibility r
Electronics Forum | Thu Apr 01 21:18:31 EST 1999 | Chris Kelly
Glenn, There are both very good VOC-Free fluxes as well as alcohol based fluxes out there. This should be your primary focus if you are so lucky as to have to opportunity to actually select a flux! The use of nitrogen will benefit any no-clean pro
Electronics Forum | Mon Oct 12 08:07:45 EDT 1998 | Earl Moon
| I have datas to substain that a not wetting PCB ( the HAL oxided or not uniform in thickness )if soldered in reflow, it shows voids with X-Ray inspection.The voids are in side all the joints not only on the solder pads levell. | | Is there a techn
Electronics Forum | Wed May 27 21:05:30 EDT 1998 | Steve Gregory
Hey yooze guys! Enough of the jokes between you and Earl (GRIN), let's get back to the topic...well, okay... you can tell a few more...(but good ones, 'kay?) Anyhoo...I'm not sure if ya'll are on the IPC Technet list or not, I've not seen any posts f
Electronics Forum | Tue May 19 05:42:36 EDT 1998 | Earl Moon
| Earl, | I admit that I missed your article since I seemed to have let my subscription to Circuit Fabrication Magazine expire. I am interested in your experience in this area. Is there a way to get a copy of your paper? Could you maybe post it to
Electronics Forum | Tue Apr 14 15:50:45 EDT 1998 | Bob Barr
Justin, Thanks for the response to my dilemma. For once it's not just me! The parts seem perfectly solderable, but I will try the modification to the profile you suggested. I wonder if the retention clips may be letting loose from the holes they a
Electronics Forum | Mon Apr 06 12:32:20 EDT 1998 | Roxanne Picou
March 31, 1998-Austin, TX --- Austin American Technology announces a new Pre-Wash feature for the Mega� II to operate in conjunction with AAT's patented closed-loop regenerative cleaning process. This feature allows for an optional dual chemistry
Electronics Forum | Fri May 17 15:50:17 EDT 2002 | davef
Now that�s a switch. Most are moving or properly have moved in the polar opposite direction. Dano, has someone been drilling your teeth lately? We use water washable flux to: * Remove solder balls. [Or put another way, we don�t have to screw-down
Electronics Forum | Thu May 08 10:16:17 EDT 2003 | davef
Observations are: * Center most lead of the fuse on the top right of the assembly looks like it has excellent solder flow, but this is PTH. From the amount of solder, it must have been wave or hand soldered. * Center most lead of the fuse on the bot