Electronics Forum | Fri Jun 05 00:08:32 EDT 2015 | acepa
Hi, I need a recommendation for a manufacturer on a reasonable cost conformal coating (silicone or other). This is a US domestic appliance PCB 9 volts only that must be dipped. Silicone or other could be unused. There is a standard RJ45 socket I wher
Electronics Forum | Thu Sep 10 17:13:31 EDT 2015 | tombstonesmt
There are factors that manufacturers have taken into consideration when dealing with coating. On/off times, dispense speeds, heights, etc.. Dedicated software with tools to easily map out paths are a godsend. We made our own coating machine with a s
Electronics Forum | Mon Oct 03 21:02:23 EDT 2016 | rwd
I am doing some rework to my CCA. I then need to conformal coat the board. I'm using Humiseal 1A33 GEL and my jumper wires are teflon coated. I understand the chemical interaction between the 2 products. My question is "Is this an acceptable prac
Electronics Forum | Mon Nov 27 13:36:41 EST 2000 | C.K.
You'd more than likely have repairability issues with the Acrylic based one. The acrylic-based finish is alot harder and more brittle versus the silicone. Some of the new silicones, you can just "peel" with your fingernail, while still getting reli
Electronics Forum | Tue Nov 28 13:26:59 EST 2000 | Graham Naisbitt
Terry Sorry, I just re-read your question and failed to answer all your questions: Shadowing only applies to coatings that are UV curable. Neither of these are UV curable. You do not want this technology for 3 dimensional assemblies, it is too expe
Electronics Forum | Fri Jan 22 10:17:47 EST 1999 | LeeAnne
I have boards coated with Humiseal 1B73. At a late point mfg. site we need to remove a series of 0603 resistors for optioning purposes. I have been trying to determine the fastest, easiest way to re-coat the pads after removal. Drying time of the coa
Electronics Forum | Wed Jan 29 13:47:32 EST 2003 | Jacob
We are currently storing small amounts of our conformal coating waste. Recently someone asked how we would dispose of the material and I hadn't the slightest idea because this is a new process for us. I started to look into proper disposal for the
Electronics Forum | Mon Jan 26 07:27:43 EST 2004 | loz
I have a product that has earthing/positioning holes, as they are to be used for earthing purposes they need to be free from conformal coating. This pcb is double sided. I have used spot/peelable mask to protect these holes. However when the conforma
Electronics Forum | Wed Oct 13 12:24:08 EDT 2004 | davef
Consider: * Equipment||Coating dip tank||Glenpro (2143 dip tank)||39 McBride Ave., Paterson, NJ 07501-1715 * Equipment||Coating dip tank||CCRCo||1954 Placentia Ave. Suite 107 Costa Mesa, CA 92627||800-443-2726 949-574-1360 Fax 1368 info@CCRCo.com ht
Electronics Forum | Thu Feb 17 10:33:53 EST 2005 | Frank R.
I use conformal coating DYMAX #984-LVUF and I don't know if it's a problem of viscosity but 0805 components are not covered properly. We use a dispensor to applied it and we cured it by UV. Even if I apply a thicker layer, the coating seems to have