Electronics Forum | Sun May 09 14:02:28 EDT 1999 | Southwest Automation Consultants
| My company has a product line that utilizes multi-up PCB's. In order to cut costs for this product line, I have been asked to look into ways of running panels that contain bad blocks. Our SMT equipment is quite capable of doing this, but I need to
Electronics Forum | Fri May 07 17:02:01 EDT 1999 | Earl Moon
| On 1.27mm (0.050 inches) Standard Ball Grid Array's. | The ball size diameter starts at approximately 0.025 inches. | | If the ball size decreases to 0.012 inches (due to the solder flowing down a via) is the solder connection reliable? | | This
Electronics Forum | Thu May 13 18:36:55 EDT 1999 | Andrew Wulff
| | On 1.27mm (0.050 inches) Standard Ball Grid Array's. | | The ball size diameter starts at approximately 0.025 inches. | | | | If the ball size decreases to 0.012 inches (due to the solder flowing down a via) is the solder connection reliable? |
Electronics Forum | Thu May 06 09:24:06 EDT 1999 | Joe Manzur
Kevin, We are also looking at printing adhesive. Our application involves printing glue on the underside of the board, once it has gone through the dip, axial & radial process. In otherwords, there are leads cut and clinched and we have to mill out
Electronics Forum | Fri Apr 23 15:33:50 EDT 1999 | C.K.
| | Has anyone had trouble waving and gluing 0603 R's and C's? At my company, our designers have "opened the floodgates" on bottom-side 0603's. | | | | We've got an EPK+ with rotary chip and omega wave but can't seem to get skip-free soldering on t
Electronics Forum | Tue Apr 20 16:41:52 EDT 1999 | Justin Medernach
| I am wondering if anyone has any info regarding solder paste misprint clean-up procedures for Entek Plus CU-106A PCB's utilizing a water-clean solder paste. In a implementation procedure they recommend a 2-3 minute wash cycle with the following cr
Electronics Forum | Mon Apr 05 08:25:31 EDT 1999 | ADRIANO FERNANDES
| | | I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | | | What disadvantages are there when using this flux? | | | Do you have any contact
Electronics Forum | Wed Mar 24 23:04:00 EST 1999 | Al O Owzitgon
| We are dealing with down time accredited to the Pumps getting clogged with dried glue. We have decided to purge all spindles at 6 hour intervals. We are looking at making this process automated. Has anybody tried this and if so, is there a way to s
Electronics Forum | Mon Mar 15 23:00:40 EST 1999 | Dave F
| In the early days, we used screens made of stainless steel or polyester. Sometimes - after A period - the tension was not good, because A wire was broken. | Later on we started to us metal stencils, glued in A polyester screen. even than we had som
Electronics Forum | Tue Mar 16 08:38:59 EST 1999 | George Verboven (Process Engineer)
| | In the early days, we used screens made of stainless steel or polyester. Sometimes - after A period - the tension was not good, because A wire was broken. | | Later on we started to us metal stencils, glued in A polyester screen. even than we had