Electronics Forum | Tue May 20 10:27:29 EDT 2008 | azimi789
I just set that as you said, but the component doesn't stick on the board. I use AMTECh Flux type: RMA-223.. what should I do ? Thanks.
Electronics Forum | Fri Dec 19 10:49:07 EST 2008 | cyber_wolf
http://www.smtnet.com/company/index.cfm?fuseaction=view_company&company_id=41853&component=mart&item_id=30111 Uhhhh....Someone (aside from us) needs to try these.
Electronics Forum | Thu May 29 13:12:10 EDT 2008 | yam6rider
Just like to know what you guys thoughts regarding mixed alloys. Production run SAC305 and some components are SAC105. So, which profile should you follow. SAC105? or SAC305.
Electronics Forum | Fri May 30 07:00:41 EDT 2008 | radizouani
What is the distance between smd components that should be held in consideration due to selective soldering ( size soldering nozzle) ? What is your advise due to the purshase a selective soldering machine.
Electronics Forum | Thu Jun 26 07:44:07 EDT 2008 | kmeline
Hello, we are having issues with two assemblies where the Melfs will lift or not solder on one end of the components. Has anyone had issues with this in the past? What can be done to help this? Thanks
Electronics Forum | Thu Jul 17 12:52:06 EDT 2008 | djd7554
We are baking the moisture out of our ic chips. They are on tape and reel. Can we bake them on tape and reel or do we have to put them in trays?
Electronics Forum | Fri Jul 25 12:54:53 EDT 2008 | schorschimi
I am interested in pwb manual assembly time standards, including hardware mounting, component preparation, hand soldering and additional tasks. Thanks for your help
Electronics Forum | Mon Jul 28 12:41:54 EDT 2008 | omid_juve
we want to estimate the price of assemblyng a board that contain both SMD and THT component . and also we have the BOM file of this board . please help me
Electronics Forum | Thu Jul 31 23:52:12 EDT 2008 | roc2x
Hi, Im having problem on tombstone, The part is LF chip component 1005, and my solder paste is WS leded. tombstone is not in a deg angle but one side is soldered but the other side is just sitting on the solder. Looks like my solder can not wick up t
Electronics Forum | Thu Jul 31 23:57:11 EDT 2008 | roc2x
Hi, Im having problem on tombstone, The part is LF chip component 1005, and my solder paste is WS leded. tombstone is not in a deg angle but one side is soldered but the other side is just sitting on the solder. Looks like my solder can not wick up t