Electronics Forum | Mon Jun 18 21:36:06 EDT 2001 | davef
Consider profiling from all of your problem components, not just your 0201.
Electronics Forum | Fri Aug 03 05:36:22 EDT 2001 | mugen
*Laughs* thats a good one Dave! me like your wicked sense of humour!
Electronics Forum | Mon Feb 07 13:40:41 EST 2000 | Dave F
Jose: Those are good guesses. Without knowing more, ask yourself: 1 There is probably adequate heat available, but that portion of the substrate that�s not soldering well is not receiving proper heating. Why is the component getting so hot, relati
Electronics Forum | Wed Jan 26 21:38:53 EST 2000 | Dave F
Dennis: I cast my vote for: poor maintenance. Ta Dave F
Electronics Forum | Tue Jan 18 12:53:50 EST 2000 | Russ
IPC 782 has package dimensions Russ
Electronics Forum | Mon Jan 03 18:52:13 EST 2000 | Deon Nungaray
Hi John, I don't know if you are going to have a lot of luck obtaining this information. Currently 0201's are mostly used in Asia, and reliability issues have risen using these components. The problem is obtaining a reliable solder connection with a
Electronics Forum | Tue Dec 21 18:09:24 EST 1999 | Brian W.
I have been soldering 0603 components on the bottom side using a glue and wave solder process for a long time. Bridging has not been a common problem. However, it is inherent on the design engineers to follow good manufacturability planning when la
Electronics Forum | Thu Nov 18 19:45:26 EST 1999 | Deon Nungaray
Deon Response: Hello Will, Yes, you can reflow a double sided board using 63/37 solder paste on both sides. There are some limitations as far as the mass of the components to reflow the second time. If you have doubts or are concerned that a compone
Electronics Forum | Fri Nov 12 13:05:36 EST 1999 | Brian W.
As a CM, I have had customers stack components as a temporary measure of incorporating an ECO. Most of the time, it includes using an adhesive to secure the component. Cost of material already in-house is the major factor when this occurs. Even th
Electronics Forum | Sun Oct 31 08:27:09 EST 1999 | Dave F
David: I think it's great that you are getting that much barrel fill with STEEL leaded components!!! So, what kind of steel are the leads are made from? How much corrosion is on the leads? Frankly, I don't believe that the leads are made of steel