Electronics Forum | Fri Mar 31 15:23:10 EST 2006 | jdumont
We have a C-740. I agree with the second pass statement. Be careful how much you overlap. Also make sure the board is very clean before you coat or its worthless. You will be able to get very accurate results without masking. Let me know if you need
Electronics Forum | Tue Apr 04 13:45:11 EDT 2006 | ultraspray
My name is Stephanie Baldwin. I work for USI and have been following this forum. I would suggest that you give both USI and Asymtek the opportunity to coat a sample board for you. You can then compare the two technologies side by side. If possibl
Electronics Forum | Tue Jan 30 14:12:12 EST 2007 | blnorman
We use nothing but silicones and have for at least the last 7 years. We don't have relays, but we do have motors. No issues with soldering, but our lines are constructed such that the last solder operation is a good distance from the coating or pot
Electronics Forum | Mon Mar 05 13:22:20 EST 2007 | blnorman
We use (and have for some time) used No-clean on our radio boards with no problems. We also conformally coat with a platinum catalyzed, addition cure silicone coating with occassional problems. These silicones are prone to cure inhibition or retard
Electronics Forum | Mon Jun 09 17:39:06 EDT 2008 | jlawson
Shadow cure effects are dealt with by post cure mechanisims. New UV Coatings should have one, either heat or moisture cure. Basically UV primary cure starts off cure process, allows handling of the products. But UV is not suitable for all products
Electronics Forum | Wed Sep 02 11:36:22 EDT 2009 | kpm135
Is this an established process that is just now exhibiting these problems, or is this a brand new process you're just setting up? What is the rest of your process like? What is done to the boards before you coat them? Water washed? Solvent washed? Sa
Electronics Forum | Thu May 20 11:36:57 EDT 2010 | davef
Ansell ANS 11-100 HYFLEX (ESD) static dissipative coated Size||Ansell p/n||Techni-Tool p/n 7||ANS111007||328PR107 8||ANS111008||328PR108 9||ANS111009||328PR109 10||ANS1110010||328PR110
Electronics Forum | Tue May 25 11:34:02 EDT 2010 | jmedernach
Hi, Use nitrile or latex gloves for handling your product from your pre-coating cleaning step onward. In my opinion, conformal coating should be isolated from the rest of the factory floor. I'm not saying you need a clean room or even a white room.
Electronics Forum | Wed Jun 16 11:49:55 EDT 2010 | tim_wright
A customer wants to coat a no-clean assembly to cut cost and cycle time. I know what wave flux I can use to make it work, but the Indium SMQ92J paste we use causes dewets. Any other no-clean pastes out there that play nice with acrylic?
Electronics Forum | Thu May 31 14:59:50 EDT 2012 | jdumont
I use Trace and certainly recommend them. I actually just had this test done last week. Adhesion test per ASTM-3359 Method B. We use Humiseal 1B73, which is similar to what you use. Is your soldermask "active" enough for this coating? I believe