Electronics Forum | Tue Nov 29 12:23:58 EST 2005 | JeffP
>Anyone can do good airflow with a little brains, and so >>delta t is important, but not the main weakness I see on >>batch convection. Actually it is a main weakness with batch and small conveyer ovens on the market. There must be a lot of people
Electronics Forum | Fri Jul 02 10:30:35 EDT 2010 | kevslatvin
We used to use an APS Gold GF-120 before we went lead-free and the HT version came out. It worked fine for low volume and proto runs though not as much control over the profile as an oven with more zones. We actually had a batch oven from Bomir befor
Electronics Forum | Fri May 15 18:13:35 EDT 1998 | Earl Moon
| | | Does the temp. profiles used to reflow double sided pcb's through a IR oven | | on FR4 board material have to be re-established if it is changed to | | polyimide? Boards will be baked out prior to assembly. | | any response would be most appr
Electronics Forum | Thu Aug 08 16:18:22 EDT 2013 | horchak
Placing and re-flowing the shield is of course the most economical. But once the shield is placed and reflowed this all but rules out inspection test and rework. Reflow should not be an issue if you have a decent forced air convection oven. You may w
Electronics Forum | Thu Dec 24 08:44:25 EST 1998 | Earl Moon
| | | | Folk's, | | | | I'm in need of some help / direction. I'm working on my thesis for a masters based on looking at the effect's of the solder resist promoting / reducing the amount of solder ball's during wave. I'm looking at thing's like colou
Electronics Forum | Wed May 12 13:34:02 EDT 2010 | hegemon
Thanks Pete B - great info. I am currently preparing a DOE to address concerns about reflow of componentry on the bottomside of the PCB while in the vapor. Specifically cosmetics and part dropping. Bottom side has no flux, but will be fully reflow
Electronics Forum | Mon Aug 25 08:15:54 EDT 2014 | jax
With a melting point of roughly 300°C, you would need to have the product see temperatures peaking around 325°C at a minimum. (I would make sure the components and PCB materials can withstand these temperatures) Most convection ovens do not go over 3
Electronics Forum | Tue Apr 17 13:33:00 EDT 2001 | Kris W
Howdy all! Nothin' up my sleeve!!! While attempting to reflow an RF antennae on std FR4, HASL coated, using no clean paste, in a Research Thermaflo 10, the part sometimes slides on one of the pads (as much as 0.125"). There is a slight amount of w
Electronics Forum | Thu Jun 11 21:30:22 EDT 1998 | Grant Petty
I am looking at purchaseing a full convection bench top oven from OK Industrys. (Model JEM-310) It seems to have all the features that we will need for low volume production runs. It has a Nitrogen input option, and I am intrested if anyone on the fo
Electronics Forum | Fri Jun 12 08:22:22 EDT 1998 | Al Carr
| I am looking at purchaseing a full convection bench top oven from OK Industrys. (Model JEM-310) | It seems to have all the features that we will need for low volume production runs. | It has a Nitrogen input option, and I am intrested if anyone on