Electronics Forum | Sun May 24 10:46:08 EDT 1998 | Dave F
> 2. Constant wrist strap monitors are ridiculously expensive. No they're value priced!!! Does anyone have a layout/BOM to build their own monitors? | Dave F
Electronics Forum | Sun May 24 08:34:36 EDT 1998 | Dave F
> 2. Constant wrist strap monitors are ridiculously expensive. No they're value priced!!! Does anyone have a layout/BOM to build their own monitors? | Dave F
Electronics Forum | Wed May 20 15:10:35 EDT 1998 | Dave F
We notice that DI water seems to tarnish or discolor the metal packaging on crystals and DIN connectors. Our marketing types like the shiney metal surfaces. We don't want to hand solder these parts after washing. Any suggestions? Dave F
Electronics Forum | Thu May 25 21:54:34 EDT 2000 | Dave F
Bernhard: I hear you, but I don't understand. What do you mean by these different philosophies? What's good and bad about them? etc etc Dave F
Electronics Forum | Thu Aug 16 05:29:29 EDT 2001 | mugen
Say din't someone previously claim, "Dave F" stands for : Damm.Averted.Verified.Eggbrain.Freakin *smart* ?!?
Electronics Forum | Thu Aug 23 00:17:53 EDT 2001 | mugen
Mike, 1) NC process = less BGA voids & void-size 2) longer soak times... Heyz, thanks mate :) ~~~~~~~~~~~~~~ Dave F, tot u were inclinded to the school of thought, that NC process hath higher chance for whining abt voids?
Electronics Forum | Sun Dec 16 04:55:33 EST 2001 | Ramanandkini
Mr.Dave.F has given an exhaustive answer. I just want to mention that some attention could be paid to the plating & contaminants on the PCB. We have experienced longer soldering time due to the presence of contaminants on the plated surface.
Electronics Forum | Fri Mar 08 11:56:17 EST 2002 | ivan
Hi Steven ,, can you please e-mail the document about cream ,at irojas@aimtronics.com ,I will be more than appreciated . And for Dave F ,,,, Thank you for the information that it make me think twice
Electronics Forum | Thu Mar 28 02:30:00 EST 2002 | ianchan
Hi Dave F, we tried to contact: 1) Jack Crawford, 2) Mel Parrish, but the (above supplied) links provided give error messages, is it possible to help relay this posting to them respectively for their help/review? thanks.
Electronics Forum | Tue Jun 18 21:07:20 EDT 2002 | ianchan
Hi mates, think between that Standard and Dave.F covers just about the "why" needs. for our side we set 40RH% to 60RH%. wonder if there is any industrial engineering basis to this setting? we do know its "optimal" for our mfg operations and envi