Electronics Forum | Wed Sep 12 17:09:11 EDT 2007 | allwave
HI John, I use wave fixtures with titanium inserts. So far I have not seen any problem with walls about 0.010" thickness and 0.120" tall (or deep depending how you see it)...The Titanium-composite interface is also very strong (as long as you have e
Electronics Forum | Mon Dec 17 02:08:21 EST 2007 | mun4o
Hi, I have a lot of solder bridge in our wave soldering process.We use SACX0307 and Surf 11 flux.the SW mashine is Vitronics delta 6622.Itry to change flux and termoprofile but results is not god.Can you halp me - recommend me some flux or other adv
Electronics Forum | Mon Dec 17 11:55:08 EST 2007 | chef
I recently had the same problems, solder bridges on every thing I made, different customers boards, etc. I wave with no-clean flux. As I sorted out problems (pin holes, blow holes, splatter, etc.) I found a lot of variable factors. I changed flux,
Electronics Forum | Mon Jul 03 05:39:05 EDT 2006 | ronalds
Hi, I am experience problems while testing wave soldering SMT components that are glued on the solderside (lead free). Between de leads of SOx type IC's and SOT's develop a great deal of solder beads. I have been using a RSS temp.profile while spr
Electronics Forum | Mon Jul 12 21:05:06 EDT 1999 | karlin
Hi, I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants) Secondly, I need also facing a lo
Electronics Forum | Fri Jan 28 12:45:14 EST 2005 | Indy
That is what we call as good "Problem Solving Skills". :)
Electronics Forum | Thu Jul 03 07:53:57 EDT 2003 | davef
That has to be the worst of all worlds. Someone goes out and buys the cheapest parts they can find, gives them to you [Loz], and wants you to assemble a perfect product. Well, it would be nice if you could console yourself by making Derick Jetter m
Electronics Forum | Thu Jul 03 03:23:04 EDT 2003 | loz
I have been advised recently about pcb manufacturers, that somehow or other supply pcb's with contamination. Visually they are fine, but problems arise during SMT manufacture, ie solder balling, non-wetting on pads, and also during wave solder proces
Electronics Forum | Thu Feb 04 09:09:07 EST 1999 | dave
Can anyone help me with the pros and cons of trying to wave solder tantalum and large (1812) ceramic capacitors. I do know that one may see fractures on larger cermaic caps, but have not seen much on the tantalums. Any insight as to what problems I c
Electronics Forum | Fri Feb 05 09:39:58 EST 1999 | Dave F
| Can anyone help me with the pros and cons of trying to wave | solder tantalum and large (1812) ceramic capacitors. I do | know that one may see fractures on larger cermaic caps, but have not seen much on the tantalums. Any insight as to what proble