Electronics Forum | Mon Mar 13 08:46:49 EST 2006 | geocominc
Yes, All six new (LF ready kit) thermocouples are tested good.I would like to say boards are populated on both side back to back with two heavy PLCC's side by side just like having heatsinks and ground plane.Some Odd design.Next try will be to have a
Electronics Forum | Thu Mar 30 13:15:31 EST 2006 | jdengler
This will depend on the feeder design. Some feeders cause a loss of several components when removing a reel from a feeder. If yours do not, the operator should be able to leave enough tape and mylar cover tape for this reel to be put back onto a fe
Electronics Forum | Wed Apr 26 07:49:49 EDT 2006 | jemills
No problems with ver 2.2 that I'm aware of. I'm in process eng. and part of my job is review the machine's capabilities. From what i read, Ver 2.3 & 2.4 software was designed to speed up setups and changeovers.I understand the auto teach functions is
Electronics Forum | Wed May 03 11:51:37 EDT 2006 | samir
Chunks, We have custom nozzles here in Riyadh that are designed to solder through-hole with SMT 0805 R's and C's just 0.5mm away. ERSA charged an arm and a leg for these, so I buy them from my toolmaker, Asadulah , for half the price. They come in
Electronics Forum | Fri Jun 09 13:31:33 EDT 2006 | Chunks
I believe this is a MELF, correct? If so, it could be your pad design. Most use a "horse shoe" style that seems to work well. Another thing to look at is your cooling zones. I've seen these parts remain liquidous into the cooling zone where they
Electronics Forum | Mon Jun 19 13:56:59 EDT 2006 | netellink
Bolos, Why you have to purchase the Titanium solder pot for your lead-free? I have the MDS-200 Unit Design Drag solder and I just empty the solder SN63PB37 in the solder pot, clean it very well and buy lead-free solder bar to fill up the pot. David
Electronics Forum | Mon Jun 12 18:44:30 EDT 2006 | muse95
OK, Pete, I just looked all through IPC-A-600G. Saw no mention of scoring anywhere. Please provide specific section number info. Thanks By the way, Chris, thank you for the information - that is really interesting stuff. Would you be willing to a
Electronics Forum | Thu Jun 15 10:00:53 EDT 2006 | Manz
Hi, I have a bad experience whenever assembling the PCBA that using SMD film capacitor as I encountered a lot of non wetting and tombstone. I did experiment on my reflow profile and stencil design and the result was improved but not totally solved.
Electronics Forum | Tue Jun 20 16:08:12 EDT 2006 | two cents
Here we go again........please do your Company and yourself a favor by listening to advice from someone other than the self proclaimed guru. Did'nt Ford think out of the box when the Edsel was designed? Good luck and make sure to check out all the al
Electronics Forum | Wed Jun 21 08:53:25 EDT 2006 | stepheniii
Are you worried the terminations might b oxidized? Do a dip test. If you have a solder pot carefully dip one termination of the cap into the solder. And see how well it wets. If that test doesn't satify the powers that be, then you can design a more