Electronics Forum | Fri Aug 26 09:57:21 EDT 2005 | russ
The Immersion gold is not a problem with BGAs specifically but "black pad" which can be present anywhere. The unfortunate thing with BGAs is you cannot see it. Personally I hate white tin. It is okay for single sided boards running no-clean, but c
Electronics Forum | Fri Aug 26 09:48:11 EDT 2005 | David
I have heard that there are problems using immersion gold on PCBs when working with BGAs. Is this correct? Is white tin more suitable?
Electronics Forum | Tue Sep 06 09:30:34 EDT 2005 | russ
I read it in Florida Cir-teks own literature. http://www.florida cirtek.com
Electronics Forum | Fri Aug 26 14:15:16 EDT 2005 | David
Where could I find more information regarding the double sided reflow and flux problems with white tin?
Electronics Forum | Wed Aug 31 12:33:25 EDT 2005 | Jaya
I have expirence running,double sided Imm gold boards recently which ed up a lot of solderability issue. The Imm gold need to be slightly more control during reflow oven area on it's profile.
Electronics Forum | Thu Jun 25 09:53:04 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | Mike, | You
Electronics Forum | Fri Jun 19 10:03:46 EDT 1998 | Earl Moon
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, We and ind
Electronics Forum | Wed Jun 24 16:23:29 EDT 1998 | Justin Medernach
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, Your concer
Electronics Forum | Wed Dec 24 15:28:17 EST 2008 | edmentzer
We use SN100C for wave soldering and hand Lead free soldering and have had very good results. The wire cored solder for hand soldering flows good and makes very good solder joints. The SN100C in the wave solder machine also works very good. We use
Electronics Forum | Tue Mar 14 07:59:41 EST 2000 | JAX
Emmanuel, The discussion on what finish to use whether it be HASL, Immersion gold over nickel, Organic Solderability Preservatives, ect...... is still ongoing. This is not the only decision you need to make. Do you plan on Soldermask Defined Pads? Wh