Electronics Forum | Tue Nov 07 14:23:13 EST 2006 | CL
Hello bpeach, We purchased a Mirtec for our first AOI machine after a side by side comparison of three different manufacturers. The Mirtec proved to be far superior to the others that we had looked at. Initially, the intention of the AOI was to prov
Electronics Forum | Fri Nov 10 17:00:05 EST 2006 | darby
Yep. If speed is not an issue a Heller 1500 will pretty well do you fine unless you are trying to process a brick. A Heller 1700 will not give you any more heated length, so don't get sucked in to that one. However, they are a little more fun to pl
Electronics Forum | Wed Dec 06 16:14:25 EST 2006 | realchunks
Assuming you meant 38 percent humidity - I would have to say your environment is only part of the problem. When you experience this problem, is because the paste has set idle for a period of time? If you knead the paste does the fine pitch print OK
Electronics Forum | Tue Nov 14 04:52:57 EST 2006 | Loco
To make it even more compicated, you have CTE before Tg and after Tg, altough the after Tg is way more important, because the expantion ratio will be much bigger, a pcb supplier will usually give the before Tg value. To come back to the delamination
Electronics Forum | Mon Dec 11 08:49:03 EST 2006 | billyd
All: Good morning. I'm writing this morning trying to find out what, right now, is the most used solder alloy out there, industry wide, for lead free applications. I'm talking strictly for reflow, not wave. I have to assume SAC305 is by fa
Electronics Forum | Sat Dec 16 14:08:32 EST 2006 | slthomas
"I did change blades and we did try another printer, problem still exists and it is across several different products but only that line." Not sure what that means since you reference "only that line" in the same phrase as "did try another printer".
Electronics Forum | Thu Dec 21 21:37:19 EST 2006 | Jack
Hi Pavel, Real Chunks, Thanks for your valuable inputs..Selecting the correct location for board profiling is critical in determining the solder joint quality. Am I right to say TC wire attachment locations priority should be as below: (1) Thermal
Electronics Forum | Mon Jan 15 03:42:08 EST 2007 | adamp
Hi all, Last week I have noticed, that solder changed colour in our Soltec wave soldering machine. I am using normal 62Sn37Pb alloy and it's colour changed to violet/darkblue with gold areas. I know that gold colour means that, there is to much Cu i
Electronics Forum | Thu Jan 25 09:56:59 EST 2007 | realchunks
Total Force is the weight on the squeegee blades. Generally you should set this by the length of blade you use. A 12 sgeegee blade would require a Total Force setting of 12 pounds. So, if you have 8 inch long squeegees, you should be OK. Your b
Electronics Forum | Mon Jan 29 10:11:12 EST 2007 | muse95
What does your customer want you to do? I would not want a CM soldering one of my boards with leadfree paste if I didn't ask him to. Whatever you do, get approval first. Two things to consider: If the other components are not rated for leadfree tem